초록
MESFETs of the Ti/Au and Ti/Pd/Au gate were fabricated on n-type GaAs. Interdiffusion at Schottky interfaces, Schottky contact properties, and MESFET characteristics with heat treatment were investigated. Ti of Ti/Au contact and Pd of Ti/Pd/Au contact acted as a barrier metal against interdiffusion of Au at >$220^{\circ}C$. Pd of Ti/Pd/Au contact acted as a barrier metal even at >$360^{\circ}C$, however, Ti of Ti/Au contact promoted interdiffusion of Au instead of role of barrier metal. As the heat treatment temperature increases, in the case of both contact, saturated drain current and pinch off voltage decreased, open channel resistance increased, and degree of parameter variation in Ti/Au gate was higher than in Ti/Pd/Au gate at >$360^{\circ}C$ Schottky barrier height of Ti/Au and Ti/Pd/Au contacts was 0.69eV and 0.68eV in the as-deposited state, respectively, and Fermi level was pinned in the vicinity of 1/2Eg. As the heat treatment temperature increases, barrier height of Ti/Pd/Au contact increased, however, decreased at >$360^{\circ}C$ in the case of Ti/Au contact. Ideality factor of Ti/Au contact was nearly constant regardless of heat treatment, however, increased at >$360^{\circ}C$ in the case of Ti/Au contact. From the results above, Ti/Pd/Au was stable gate metal than Ti/Au.