Strength and Reduction Behaviour of Cold-bonded Pellet for Blast Furnace Burden using Iron-bearing Dust

함철 더스트를 원료로 한 고로용 비소성 펠릿의 강도 및 환원거동

Iron-bearing dust which stems from steelworks were pelletized and bonded with portland cement in order to attempt to use for blast iurnace burdens. The characterist~cs of cold bonded dust pellet were investigated. It was found that the compression strength of cold bonded pellet contaning portland cement of 10 wt.% reached above 150kg/p by proper curing treatment. Direcl contad of carbon with iron oxides seems to greately enhance a reduction reaction and herewxth increased chances to lorn pores at high temperature environment. Tumbler strength, RDI, and swelling of cold bonded pellet were similiar to and/or better than those of iron ore sinter and fired pellet.

철강공정에서 발생하는 함철더스트에 시멘트를 첨가한 비소성 더스트 펠릿을 제조하여 고로용으로서의 특성을 평가하였다. 시멘트를 10wt.% 첨가한 펠릿은 적절한 양생조건하에서 150kg/p 이상의 압축강도에 도달하였다. 더스트 펠릿은 특히 $900^{\circ}C$에서의 환원성이 우수하였는데, 이는 비소성 펠릿 중에 함유된 탄소의 직접환원 반응과 고온에서 증가된 기공 때문이다. 이외에 비소성 펠릿의 회전강도, 환원분화성 및 환원 팽창성도 철광석 소결광 및 소성 펠릿에 비교하여 우수하거나 대등한 성상을 나타내는 것을 확인하였다.