Production of Fine Cobalt Metal Powders from Superalloy Scrap(1) (Treating Superalloy Scrap with Zinc)

Superalloy 스크랩으로부터 Co 미분말의 제조(1) (Superalloy 스크랩의 아연처리)

Treating bulk superalloy scrap with molten zinc has been studled to facililate recycling and recovery- of cobalt.Superalloys investigated were the cobalt-base Mar-M-509 and X45 and the nickel-base Rene 80. Charges withZnlscrap ratlos of 1.5-6.5 were heated to 750-9002 far 1-7.5 hours in a nitrogen atmosphere. The moltenzinc dissolved superalloy scrap and zinc was removed by vacuum distillation at 850-Wk for 4-6 hours. Ithas been concluded that the optimum conditions of decomposition for Mar-M-509 and Rene 80 \"ere dissolutiontemperature of about 850k, Znlscrap ratlo of about 5, and dissalution time of about 5.5 hours. The zinc-treatedsuperalloy prouducts were friable and reacted rapidly with acid solutions. Leaching 9mm pieces of unalloyedMar-M-509 or Rene 80 with 5 times the stolchlometric amount oi 6N HCI at 90t ior 3 hours dissolved about1.5-7.270, while leachmg of the minus 20-mesh products dissolved about 89.0-93.0%.ved about 89.0-93.0%.

Co의 리싸이클링을 원활히 하기 위하여 괴상 superalloy 스크랩을 용융Zn으로 분해할 때의 최적처리조건을 조사하였다. 조사한 superalloy는 Co-기 Mar-M-509와 X-45 그리고 Ni-기 Rene 80이었다. Zn/스크랩 비율이 1.5~6.5인 장입물을 질소 분위기에서 $750~900^{\circ}C$에서 1~7.5시간 동안 가열하였다. 용융된 Zn은 스크랩을 용해하였고, Zn은 $850~900^{\circ}C$에서 4~6시간 동안 진공증류하여 제거되었다. Mar-M-509와 Rene 80의 최적 처리조건은 용해온도 약 $^850{\circ}C$, Zn/스크랩 비율 약 5, 그리고 용해시간 약 5.5시간이었다. Zn처리 superalloy 생성물은 쉽게 부스러졌으며, 산 용액에 의해 빠르게 침출되었다. Mar-M-509 또는 Rene 80의 경우, 미처리 스크랩(9mm 조각)을 화학양론양 5배의 6N HCl으로 $90^{\circ}C$에서 3시간 동안 처리하면 침출도는 약 1.5~7.2%에 지나지 않았으나, Zn처리 생성물(-20 메쉬의 것)의 침출도는 약 89.0~93.0%나 되었다.