A Study on the Leaching of Gold and Silver from Concentrate by Acidothiouration

산성치오요소법에 의한 금정광으로부터 금, 은의 침출에 관한 연구

The dissolution of gold and silver from concentrate was studied with acidic thiourea solution. The results showed that the gold and silver extraction was severely affected by concentration of thiourea and oxidant, pulp density, etc. Especially, oxidant such as ferric ions enhanced the leching rate of gold and silver. High concentration of ferric ions, however, dissolved the sulfide ore to form electrochemically passive layer on the surface of ore particles, which caused the precious metal not to be leached out from the ore. The use of $SO_2$could not effectively enhance the recovery of precious metal but reduce to some extent the consumption of thiourea. The leaching of gold and silver was achieved with recovery more than 90% and 80%, respectively, under the following conditions; Thiourea conc. :0.4M Oxidant : None $H_2SO_4$ conc. : 0.5M Pulp density : <10% Leaching time :4 Hrs Potential :250mV The Thiourea was consumed about 10% in comparison with its initial concentration.

국내의 금정광으로부터 산성치오요소법에 의해 금, 은을 회수하기 위한 침출실험을 행하였다. 실험결과에 따르면 금, 은의 침출은 치오요소 및 산화제의 농도, 광액농도 등에 의해 크게 영향을 받고 있으며, 특히 3가철과 같은 산화제는 금, 은의 침출속도를 상당히 증가시킨다. 그러나 3가철의 농도가 너무 높으면 황화팡을 용해시켜 광석입자표면에 부동태층을 형성하기 때문에 금, 은의 침출을 저해하기도 한다. 한편 침출반응시 $SO_2$를 첨가하면 치오요소의 소모량은 어느정도 절감시킬 수 있으나, 금은의 침출율이 저하하여 귀금속의 회수에는 그리 효과적이지 못하다. 금정광으로부터 금과 은은 적정조건하에서 각각 90% 및 80%의 침출율을 보이며 이때 치오요소 소모량은 초기 농도의 약 10% 정도이다.