Synthesis of High Purity Tungsten Oxide with Tungsten Chloride from the Chlorination of Scheelite

회중석의 염소화 생성물로부터 고순도 WO3의 합성

  • 엄명헌 (천안공업전문대학 공업화학과) ;
  • 박용성 (단국대학교 공과대학 화학공학과) ;
  • 이철태 (단국대학교 공과대학 화학공학과)
  • Received : 1993.07.23
  • Accepted : 1993.08.18
  • Published : 1993.09.01

Abstract

In this study we developed the synthesis of high purity tungsten oxide from tungsten chlorides obtained by the chlorination of scheelite in a fluidized bed reactor. Within a minute of dissolution time, tungsten chlorides were almost dissolved in $H_2O_2$ solution. The proper dissolution conditions for the tungsten chlorides were as follows : $H_2O_2$ concentration 0.5%, dissolution temperature $15^{\circ}C$ and $H_2O_2$ amount to 0.5g tungsten chlorides 30ml. Under above conditions, the tungsten oxide prepared from dissolved product was identified as $WO_3$ and the purity of $WO_3$ was 99.53%.

본 연구는 유동층 반응기에서 회중석의 염소화 생성물인 텅스텐염화물로부터 고순도 tungsten oxide를 합성하기 위해 수행하였다. 텅스텐염화물은 용해시작 불과 1분 이내에 거의 완전히 $H_2O_2$ 용액에서 용해되었으며 적정용해조건은, $H_2O_2$의 농도 0.5%, 용해온도 $15^{\circ}C$, 텅스텐 염화물 0.5g에 대한 $H_2O_2$용액의 양은 30ml이었다. 이 조건하에서 얻어진 용해 생성물로부터 제조되어진 텅스텐 산화물은 순도 99.53%의 $WO_3$였다.

Keywords