Abstract
As a result of adsorbing phthalocyanine (metal free, ${\alpha}\;and\;{\beta}$-Cu) on zinc oxide in aqueous solution using nonionic surfactant, all of the added dye was adsorbed and Na salt of sulfonated phthalocyanine showed the Langmuir monolayer adsorption. To analyze the effect of adsorption on zinc oxide, photovoltage was measured using surface photovoltmeter. The high photovoltaic effect was observed at intrinsic wavelength of zinc oxide and wavelength of adsorbed phthalocyanine dye. Metal free phthalocyanine, ${\alpha}$-copper phthalocyanine and ${\beta}$-copper phthalocyanine showed the highest photovoltaic effect when the percentage of coverage (${\theta}_{BET}$) for zinc oxide is about 80, while sulfonated phthalocyanine showed the highest photovoltaic effect when the percentage of coverage for zinc oxide is about 30.
${\alpha},{\beta}$-구리 및 무금속의 프탈로시아닌을 비이온성 계면활성제를 사용하여 수용액 중에서 산화아연에 흡착시켰더니, 첨가시킨 색소가 모두 흡착되었다. 계면활성제를 사용하지 않고 술폰화된 프탈로시아닌의 나트륨염인 경우는 Langmuir 단분자 흡착성을 나타내었다. 흡착상태에 따른 증감특성을 알기 위하여 진동용량형 표면 전위계를 사용하여 광기전력을 측정하였더니, 산화아연의 고유파장과 프탈로시아닌 색소의 흡수파장에서 높은 광기전력을 나타내었다. 계면활성제를 이용하여 흡착시킨 프탈로시아닌은 산화아연에 대한 피복율(${\theta}_{BET}$)이 약 80%에서 광기전력이 크게 나타났고, 술폰화된 프탈로시아닌은 피복율(${\theta}_{BET}$)이 약 30% 부근에서 광기전력이 증가하는 경향을 나타내었다.