Development of New Biocompatible Fiber form Composite of Chitin and Cellulose

카틴과 셀룰로우스의 복합체로부터 새로운 생체흡수성 봉합사의 개발

Chitin-based fibers have low mechanical strength and hence cannot be used as surgery fiber due to fast degradation In tissues. A new fiber Chitulose was made by mixing chitin with cellulose, both of which have similar structure. A mixture of dimethylacetamide (DMAc) and 6% lithium chloride (LiCl) was found to be an effective solvent system for dissolvoing chitin and cellulose. The Chitulose fiber made by wet spinning of a mixture of chitin and cellulose resulted in the highest degree of strength and flexibility when the ratio of chitin to cellulose was 1.5; 0.2. The fiber maintained mechanical structure even after autoclaving, indicating thermal stability. A biodegradability test of the Chitulose fiber by imbeding in a rat showed that degradation was initiated in 14 days and completely done in 40 days.

Chitin 섬유는 인장강도가 기대치 보다 약하며 생 체조직 내에서 흡수도가 너무 빨라 수술 후 2주일 정도의 강도 유지밖에 못하는 단점 등이 었으므로, chitin과 그 구조가 비슷한 cellulose와 혼합하여 인 장력과 유연성이 크게 증대된 Chitulose 섬유를 개 발하였다. 우선 chitin과 cellulose가 잘 용해되어 혼 합펼 수 있는 용매로서 DMAc/LiCl을 탐색하였으며 이 용애계에 용해시킨 Chitulose 용액을 가지고 습 식방사하여 얻은 Chitulose 섬유 중, 용매에 대한 chitin cellulose 함량비가 1.5: 0.2얼 때, Instron 시험결과 강도와 유연성이 가장 좋았으며, 멸균시 autoclave해도 변화되지 않아 열에 매우 안정한 것 으로 나타났다. 이 섬유를 가지고 400-500g되는 백서의 피하조직에 매몰시킨 후, 생체 내 분해흡수 도를 관찰한 결과, 매볼 후 14일부터 분해되기 시작 하여 40일 후에는 완전히 분해흡수되였다.