Development of New Biodegradable CHITULOSE film from Composite of Chitin and Cellulose

Chitin과 Cellulose 복합체로부터 새로운 생분해성 CHITULOSE film의 개발

A Chitulose film was made by dissolving chitin and cellulose in a dimethylacetamide/LiCl solvent system This film was completely degraded in 20 days in soil and penetrated by soil microorganisms in 16-26 hours. A permeability analysis of the film showed that water permeability was in the range of 0-187.5 $1/m^2$/day, depending upon the ratio of chitin to cellulose and decreased with increasing a cellulose content in the Chitulose film The permeabilities of organic compounds, $Na^+$ and oxygen change with the composition of the Chitulose file The film was tested with a burned 2~3degree rat for exploring its use as artificial skin. The rat was completely cured within 31 days without inflammation.

Chitin과 cellulose를 dimethylacetamide/LiCl 용매에 용해시켜 유리판 위에서 Chitulose film을 제조 하였다. 이 film은 토양속에서 20일 후에 거의 분해 되었고, 토양 미생물을 16-26hr 후에 투과시켰다. 한편, 필름의 투과도를 검토해 본 결과 물의 투과도는 Chitulose film에서 chitin, cellulose의 혼합 비율에 따라 0~187,500ml/$m^2$/day로 cellulose 함량이 높을 수록 투과도가 낮게 나타났으며, 풍건보다는 중탕에 의한 필름건조방법으로 제조된 것이 우수하였다. 각종 유기물의 최대, 최소투과도는 Chitulose film 의 종류에 따라 달리 나타나 chitin과 cellulose의 조성에 따라 선택적 투과성을 나타내였다. $Na^+$ 이온에 대한 투과도도 달리 나타나 보였고, 산소 투과도도 역시 Chitulose film의 조성에 따라 14-17,850 c $cm^3/m_2$/day로 큰 차이를 보였다. 2~3도 화상을 입힌 쥐에다 Chitulose film을 인조피부로 사용한 결과 염증없이 14일 후에 딱지가 떨어졌고, 31일 후에 완치되는 것이 관찰되었다.