The Thermal Reaction and Oxygen Behavior in the Annealed TiN/Ti/Si Structures

열처리에 따른 TiN/Ti/Si 구조의 열적반응 및 산소원자의 거동에 관한 연구

We have investigated the thermal reaction property and the oxygen behavior of TiN/Ti/Si structure after different hear treatments using x-ray photoelectron spectroscopy and cross-sectional transmission electron microscopy measurements. During the heat treatment in N$_2$ amibient, the considerable amount of oxygen atoms incorporates into TiN/Ti/Si Structures. It is found that oxygen atoms pile up at the top surface of TiN and TiN/Ti interface, forming a compound of TiO$_2$ above $600^{\circ}C$. Inside the TiN film, the oxygen content increases as the annealing temperature increases, mostly TiO and Ti$_2$O$_3$ rather than thermodynamically stable TiO$_2$. Above the annealing temperature of 55$0^{\circ}C$, the TiSi$_2$ formation has initiated. One thing to note is that a severe blistering is observed in the sample annealed at $600^{\circ}C$, due to (1) the difference of thermal expansion coefficient between TiN and Si` (2) the compressive stress induced by the volume reduction caused by the Ti-Silicide grain while elevating temperatures.