Abstract
The shrinkages and physical properties of silk yarn were studied on the effect of treatment concentration, time and temperature with various neutral salts. The degummed silk yarn was shrunk about 35 percent by highly concentrated solution of Ca(NO3)2 on conditions of S.G.(special gravity) 1.45 at 9$0^{\circ}C$ or S. G. 1.46 at 8$0^{\circ}C$. About 40 percent of silk yarn was contracted in length by the treatment of CaCl2 solution on conditions of S. G. 1.33 at 9$0^{\circ}C$ for 5 mins. or at 85$^{\circ}C$ for 10 mins. By treating the concentrated solution of LiBr the silk yarn showed about 40 percent of shrinkage on a conditions of S. G. 1.38, $25^{\circ}C$ 24hrs. The physical properties of salt-treated silk yarn could be significantly changed with shrinkage variations. There were some differences in shrinkages between different type of salts. However, it was observed that generally the tenacity was decreased and breaking elongation increased as the shrinkage increased. The bulkiness of salt-treated silk yarn was increased by 110 to 120 percent compared with untreated yarn.
견사에 대한 실용적인 염축조건 구명을 위하여 3종 중성염류의 처리농도시간 및 온도조건이 처리견사의 수축율 및 물성에 미치는 영향을 검토한 결과 1. Ca(NO3)2의 처리조건, 비중 1.45, 9$0^{\circ}C$ 또는 비중 1.46, 8$0^{\circ}C$에서 견사의 수축율이 35% 내외였다. 2. CaCl2는 비중 1.33, 9$0^{\circ}C$, 5분 또는 85$^{\circ}C$ 10분의 처리조건에서 견사의 수축율이 40% 내외였다. 3. LiBr은 비중 1.38, $25^{\circ}C$ 24시간 처리에서 견사의 수축율 40% 내외였다. 4. 수축율 증가는 여러 가지 물리적 성질변화를 가져오는데 3종의 중성염류에 따라 변화율은 다소 차이가 있으나 강도의 감소가 현저히 나타나며 신도는 증가하는 추세를 나타내었다. 5. 염축견사의 팽화도는 미처리견사에 비하여 100% 이상 향상되었으나 처리견사의 강력은 미처리견사의 반 정도로 감소되었다.