초록
The standrd electrolyte for the electrodeposition of chromium were preparwith reagent grade chromic acid(200g/L), sulfuric acid(pH=1.8)and oxalic acalic acid(640g/L)as additive. Carbon content in chromium plating varied about2.0-3.8 wt% with current density and temperatures of the bath. The hardeness of chromium platings incresed with increasing the annealing temperatures and showed maximum value of about Hv 1700 after annealing at$ 700^{\circ}C$for 60min. But, decreased it as annealing at above $700^{\circ}C$. The reason for varing thee hardness of chromium codeposited with carbon gradually foumed chromium carbide(Cr7C3), but that changed to Cr23C6 as annealing temperature at above $^700{\circ}C$. The X-ray diffraction pattern indicated that chromium carbides, such as Cr7C3 or Cr3C2, formed at formed at above $300^{\circ}C$. titanium coating sputtered on the on surface of chromium plating had performed and determined the hardness after annealing at 500, 600, $700^{\circ}C$ for 60min. the maximum hardeness was about Hv 2400 as annealing at $700^{\circ}C$. The titanium carbide formed in layer was identified by X-ray diffraction. It was confirmed that chromium and titanium carbide has effect of increasing the hardness.