Abstract
The crystallization behaviours of poly(ethylene terephthalate) modified by 1, 3-propane diol, 1, 5-pentane diol, 1, 6-hexane diol, or poly(ethylene glycol) of molecular weight 300 as a third component were studied by isothermal and nonisothermal crystallization. When the content of the third diol was about 4 mol %, the isothermal crystallization rate at the same supercooling below the melting temperature and the nonisothermal crystallization rate at the same overheating above the glass transition temperature were increased more by the shorter flexible diol unit. On the contrary the nonisothermal crystallization rate at the same supercooling below the melting temperature was increased more by the longer flexible diol unit.
1,3-propane diol, 1,5-pentane diol, 1,6-hexane diol, 분자량이 300인 poly(ethylene glycol)등을 제 3의 디올로 사용하여 poly(ethylene terephthalate)를 개질하여 개질된 copolyester의 결정화 거동을 비교하였다. 개질된 copolyester 중 제 3의 디올 함량이 약 4몰%인 경우 유리전이온도 부근에서 승온시키면서 유리전이온도로 부터 일정 온도 위에서의 결정화 속도를 비교하거나, 녹는점 부근에서 등온 결정화시켜 동일 과냉각 상태에서의 결정화 속도를 비교하면 가해진 디올의 길이가 짧을수록 결정화 속도가 크게 촉진되었다. 이에 반해 녹는점 부근에서 강온시키면서 동일 과냉각 상태에서의 결정화 속도를 비교하면 가해진 디올의 길이가 길수록 결정화 속도가 크게 촉진되었다.