Diffusion Characteristics for Chloride Ion of Concrete Subjected to Sulfate Attack

황산염 침투를 받은 콘크리트의 염소이온 확산특성

  • 박재임 (안동대학교 토목공학과) ;
  • 배수호 (안동대학교 토목공학과) ;
  • 유재원 (안동대학교 토목공학과) ;
  • 이광명 (성균관대학교 사회환경시스템공학과)
  • Published : 2010.05.06

Abstract

An objective of this experimental research is to investigate the diffusion characteristics for chloride ion of concrete subjected to sulfate attack. For this purpose, concretes with three types of cement such as ordinary portland cement(OPC), binary blended cement(BBC), and ternary blended cement(TBC) containing mineral admixtures were made for water-binder ratios of 32% and 43%. The concrete specimens were immersed in sulfate solution for 365 days, and then the resistance against chloride ion penetration of them were estimated by using NT BUILD 492. It was observed from the test results that the resistance to chloride ion penetration of concrete subjected to sulfate attack was greatly decreased than that of standard curing concrete under the same age.

본 연구의 목적은 황산염 침투를 받은 콘크리트의 염소이온 확산특성을 평가하는 것이다. 이를 위하여, OPC, 2성분계 및 3성분계 시멘트를 혼입한 3가지 형태의 콘크리트를 물-결합재비 32% 및 43%에 대해서 제작하였다. 제작한 콘크리트 시험체를 365일 동안 황산염 용액에 침지시킨 후 NT BUILD 492에 의해 염소이온 침투 저항성 시험을 수행하였다. 그 결과, 황산염 침투를 받은 콘크리트는 동일 재령의 표준양생 콘크리트보다 염소이온 침투 저항성이 크게 저하되는 것으로 나타났다.

Keywords