Fabrication and effect of different temperatures on the supported thin Anode for molten carbonate fuel cell

용융탄산염 연료전지에서 지지체를 사용한 얇은 연료극의 제작과 각기 다른 온도에서의 영향

Recently, Molten carbonate fuel cells(MCFCs) have been developing to get a good durability and economic feasibility for commercialization. To achieve these objectives, the cost of nickel based electrodes should be reduced. Regular anode thickness used in MCFCs is normally 0.7mm. Thus, in our study, the purpose was to reduce anode thickness up to 0.3 mm keeping MCFC performance on standard levels. In-situ sintering has been used, with 2 different fabrication methods (method A and B) and 2 different supports (support 1 and 2). Voltage losses at different temperature (600,620,640,$650^{\circ}C$) and after 1000 hours showed the higher performance that can be obtained using method B and support 2. After single cell test, an open-circuit voltage(OCV) of 1.075 V and a closed-circuit voltage(CCV) of 0.829V were obtained, at current density of $150mV/cm^2$. Also the voltage loss ratio at different cell temperature was lower in the case of method B and support 2. According to these results, the cost of anode fabrication can be reduced in the future, contributing for the economical feasibility of MCFCs.