Abstract
This is for the electrical characterization by IDC pattern using BST$(Ba_{0.5}Sr_{0.5}TiO_3)$ thin film. BST materials had been chosen for high frequency applications due to it's high permitivity and tunability. The BST thin films have been deposited on $Al_2O_3$ Substrates by Nd-YAG pulsed laser deposition with a 355nm wavelength at $700\;^{\circ}C$. The post deposition annealing at $750^{\circ}C$ in flowing $O_2$ atmosphere for 1 hours. The capacitance of IDC patterns have been measured from 1 to 10 GHz as a function of electric field ($\pm40$ KV/cm) at room temperature using inter-digital Au electrodes deposited on top of BST. The IDC patterns have three type of fingers number. For the 10 pairs finger was the best capacitance onto $Al_2O_3$ substrate. The capacitance was 0.9pF. Also Dielectric constant was been 351 at 100 mTorr and annealing temperature $750^{\circ}C$ for 1 hour. The loss tangent was been 0.00531.