The Experimental Study on The Compressive Strength of Concrete Using High Quality Recycled Fine Aggregate Produced by Sulphuric Water and Low Speed Wet Abrasional

황산수와 저속습식마쇄기로 생산된 고품질 순환 잔골재의 콘크리트 압축강도에 관한 실험적 연구

Recycled fine aggregate has low quality because it contains large amount of old mortar. So, its usage is limited to a lower value-add, such as the roadbed material etc. Also, alkaline water occurred from treatment process of the waste concrete is becoming the cause of environmental problem. Accordingly, this study is to develop on the high quality recycled fine aggregate produced by low speed wet abraser using sulphuric. We investigated the properties of compressive strength of the mortar which was manufactured using recycled fine aggregate containing calcined gypsum produced by earlier mentioned process. Test results indicate that concrete using recycled fine aggregate containing calcined gypsum is higher compressive strength than concrete using other sands.

현 국내에서 생산되고 있는 대다수의 순환잔골재는 골재표면에 부착되어 있는 구모르터 성분으로 인하여 낮은 밀도와 높은 흡수율의 물리적 특성을 나타내는 저품질 골재이다. 이러한 이유로 일반 콘크리트용 골재 또는 콘크리트 제품제조용 골재로 사용이 부적합하며 일반 성토, 매립재용으로 사용되고 있는 실정이다. 또한 골재 세척에 사용되는 공정수는 골제 세척 후 강알칼리성을 띠게 되어 추가적인 처리비용이 발생한다. 이러한 문제점을 해결하기 위하여 기존 파 분쇄 방법이 아닌 마쇄 방법을 사용하여 골재간의 마찰과 자유낙하에 의한 운동에너지로 골재표면에 구모르터 성분을 탈리시키고 황산수를 공정수로 사용함으로써 중화반응에 의해 중성 또는 약산성화 하는 방법으로 고품질 순환잔골재를 생산하였다. 상기의 방법으로 생산된 순환 잔골재는 구모르터 성분에 포함되어있는 수산화칼슘($Ca(OH)_2$)과 공정수에 투입한 황산($H_2SO_4$)의 중화반응에 의해 반응생성물인 석고가 생성되고, 중화반응에 의해 생성된 석고는 재생골재를 건조하는 과정에서 반수석고로 변환된다. 일반적으로 시멘트에 포함된 석고는 응결을 완화 할 뿐 아니라 단기강도를 높이고 건조수축을 감소시키며, 화학적 저항성을 향상시키는 등의 효과가 알려져 있다. 이에 본 연구는 저품질의 순환잔골재를 황산수와 습식마쇄방법을 이용하여 고품질의 순환잔골재로 생산한 후 이를 콘크리트에 적용하였을 때 반응생성물질인 반수석고가 콘크리트의 압축강도에 미치는 영향에 대하여 검토하였다. 실험 결과, 반수석고가 포함된 순환잔골재를 사용한 콘크리트가 압축강도가 가장 높게 나타났고 휨강도는 석고를 제거한 순환 잔골재를 사용한 콘크리트가 가장 높게 나타났다.