Growth and temperature dependence of energy band gap for $CuAISe_2$ Single Crystal Thin Film by Hot Wall Epitaxy

Hot Wall Epitaxy(HWE)법에 의한 $CuAlSe_2$ 단결정 박막의 성장과 에너지 밴드갭의 온도 의존성

Single crystal $CuAlSe_2$ layers were grown on thoroughly etched sem-insulating GaAs(l00) substrate at $410^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $CuAlSe_2$ source at $680^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $CuAlSe_2$ thin films measured with Hall effect by van der Pauw method are $9.24{\times}l0^{16}\;cm^{-3}$ and $295\;cm^2/V{\cdot}s$ at 293K, respectively. The temperature dependence of the energy band gap of the $CuAlSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;=\;2.8382\;eV\;-\;(8.68\;{\times}\;10^{-4}\;eV/K)T^2/(T\;+\;155\;K)$.