Characterization for $AgGaS_2$ single crystal thin film grown by hot wall epitaxy

Hot Wall Epitaxy(HWE)법에 의해 성장된 $AgGaS_2$ 단결정 박막의 특성

A stoichiometric mixture of evaporating materials for $AgGaS_2$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films. $AgGaS_2$ mixed crystal was deposited on thoroughly etched semi-Insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $590^{\circ}C$ and $440^{\circ}C$, respectively. The temperature dependence of the energy band gap of the $AgGaS_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=2.7284 eV-(8.695{\times}10^{-4} eV/K)T^2/(T+332 K)$. After the as-grown $AgGaS_2$ single crystal thin films was annealed in Ag-, S-, and Ga-atmospheres, the origin of point defects of $AgGaS_2$ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K.