In this study, (La,Sr)$MnO_{3+\delta}$ powder used cathode material for SOFC was synthesized with precursor by GNP and the properties of powder, crystal phase, electric properties and deoxidization properties with precursor were investigated. The synthesis powder was prepared when oxidant/fuel mole and pH were 1 and 1, respectively and the synthesis powder was synthesized by GNP method using nitrate solution or oxide solution as precursor. Deoxidization peak of the nitrate solution was appeared lower temperature than the oxide solution, at $450^{\circ}C$. In this result, synthesis (La,Sr)$MnO_{3+\delta}$ powder using nitrate solution with Mn excess was suitable cathode material for SOFC due to had higher deoxidization properties. Also synthesis (La,Sr)$MnO_{3+\delta}$ powder according to precursor had difference electrical conductivity according to influence sintering density and crystal phase with precursor. Specially, the synthesis method and starting material had effect on deoxidization properties for SOFC.