Piezoelectric Properties and phase transition of $KNbO_3$ Ceramics with B-site substitution

(K,Na)$NbO_3$세라믹스에서 B-site의 Sb 치환에 따른 압전 특성 및 상전이 거동

  • Lee, Moon-Seok (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Lee, Yong-Hyun (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Bang, Je-Myong (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Suk, Jong-Min (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Choi, Jong-Bum (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Cho, Jeong-Ho (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Kim, Byung-Ik (Advanced Materials and Components Lab, Korea Institute of Ceramic Engineering and Technology) ;
  • Shim, Kwang-Bo (Department of Ceramic Engineering, Hanyang University)
  • Published : 2005.11.10

Abstract

[ $(K_{0.5}Na_{0.5})NbO_3$ ](KNN) 세라믹스의 소결 특성과 압전 특성을 높이기 위해 B-site에 Sb를 치환하여 Sb함량에 따른 특성을 측정 하였다. Sb 의 함량을 0mol $\sim$ 0.1mol 까지 첨가한 결과 소결 밀도는 Sb의 첨가량이 많아질수록 증가하다 Sb-0.08mol에서 4.40g/$cm^3$으로 가장 높은 밀도를 가졌으며, 여기서의 전기기계 결합 계수가(Kp) 0.45로 높은 값을 나타내었다. 상전 이 온도는 375$^{\circ}C$로 순수한 KNN 의 420$^{\circ}C$ 보다 약 45$^{\circ}C$정도 떨어졌으나 orthorhombic에 서 tetragonal 로 바뀌는 전이 온도는 KNN이 220$^{\circ}C$, KNNS 가 225$^{\circ}C$로 크게 변하지 않았다.