Study on the viscoelasticity properties of EBA/Carbon Black composites by temperature changes

온도 변화에 따른 EBA/카본블랙 복합체의 점탄성 특성에 관한 연구

To measure elastic properties of semiconducting materials in power cable, we have investigated modulus of EBA/carbon black composite showed by changing the content of carbon black. The specimen was primarily kneaded in material samples of pellet form for 5 minutes on rollers ranging between 70[$^{\circ}C$] and 100[$^{\circ}C$]. Then this was produced as sheets after pressing for 20 minutes at 180[$^{\circ}C$] with a pressure of 200[kg/cm]. The contents of conductive carbon black were 20, 30 and 40[wt%], respectively. The modulus experiment was measured by DMA 2980. The ranges of measurement temperature were from -50[$^{\circ}C$] to 100[$^{\circ}C$] and measurement frequency is 1 [Hz]. The modulus of specimens was increased according to an increment of carbon black content And modulus was rapidly decreased at the glass transition temperature. The tan$\delta$ of specimens was decreased according to an increment of carbon black content.