Abstract
The a-Si:H TFT using ferroelectric of SrTi $O_3$as a gate insulator is fabricated on glass. Dielectric characteristics of ferroelectric are superior to $SiO_2$and S $i_3$ $N_4$. Ferroelctric increases on-current, decreases thresh old voltage of TFT and also improves breakdown characteristics. The a-SiN:H has optical band gap of 2.61 eV, refractive index of 1.8~2.0 and resistivity of 10$^{13}$ - 10$^{15}$ $\Omega$cm, respectively. Insulating characteristics of ferroelectrics are excellent because dielectric constant of ferroelectric is about 60~100 and breakdown strength is over 1MV/cm. TFT using ferroelectric has channel length of 8~20${\mu}{\textrm}{m}$ and channel width of 80~200${\mu}{\textrm}{m}$. And it shows that drain current is 3.4$mutextrm{A}$ at 20 gate voltage, $I_{on}$ / $I_{off}$ is a ratio of 10$^{5}$ - 10$^{8}$ and $V_{th}$ is 4~5 volts, respectively. In the case of TFT without ferroelectric, it indicates that the drain current is 1.5 $mutextrm{A}$ at 20 gate voltage and $V_{th}$ is 5~6 volts. With the improvement of the ferroelectric thin film properties, the performance of TFT using this ferroelectric has advanced as a gate insulator fabrication technology is realized.zed.d.