Abstract
This study is performed to evaluate the strength and nan-fracture test of the ready mixed concrete(RMC) using polypropylene. The slump is reached in $8{\pm}2cm$ of each RMC using polypropylene or without polypropylene, air content is reached in $4.5{\pm}1.5%$, the chloride content is below $0.3kg/m^3$. The compressive strength of RMC not using polypropylene is appeared over $210kgf/cm^2$ at the curing age 7 days and $239kgf/cm^2$ at the curing age 28 days. The compressive strength of RMC using polypropylene is appeared over $188kgf/cm^2$ at the curing age 7 days and $238kgf/cm^2$ at the curing age 28 days. The dynamic modulus of elasticity of RMC not using polypropylene is appeared over $298{\times}10^3kgf/cm^2$ at the curing age 7 days and $342{\times}10^3kgf/cm^2$ at the curing age 28 days. The RMC using polypropylene is appeared over $284{\times}10^3kgf/cm^2$ at the curing age 7 days and $238{\times}10^3kgf/cm^2$ at the curing age 28 days. The pulse velocity of RMC not using polypropylene is appeared over 4,198m/s at the curing age 7 days and 4,382m/s at the curing age 28 days. The RMC using polypropylene is appeared over 4,182m/s at the curing age 7 days and 4,342m/s at the curing age 28 days.