Pyroelectric Properties of PZT System Ceramics with Addition of $Y_2O_3$

$Y_2O_3$ 첨가에 따른 PZT계 세라믹의 초전특성

  • Published : 2003.11.13

Abstract

In this paper, $0.10Pb(Sb_{1/2}Sn_{1/2})O_3-0.25PbTiO_3-0.65PbZrO_3$ ceramics were fabricated by the mixed-oxide method. The sintering temperature and time were $1230^{\circ}C$ and 2(hr), respectively. The structural, dielectric and pyroelectric properties with addition of $Y_2O_3$ were studied. The crystal structure of a specimen was rhombohedral. As a result of SEM, the average grain size were decreased with increasing the contents of $Y_2O_3$. Relative dielectric constant and dielectric loss of the specimen doped with 0.2wt% $Y_2O_3$ were 597 and 0.022, respectively. Remanent polarization and coercive field of the specimen doped with 0.4wt% $Y_2O_3$ were $8.5[{\mu}C/cm^2]$ and 10.2[kV/cm], respectively.