Abstract
Thickness dependence of crystallographic orientation of diol based sol-gel derived PZT(52/48) films on dielectric and piezoelectric properties was investigated The thickness of each layer by one time spinning was about 0.2 $\mu\textrm{m}$, and crack-free films was successfully deposited on 4 inches Pt/Ti/SiO$_2$/Si substrates by 0.5 mol solutions in the range from 0.2 $\mu\textrm{m}$ to 3.8 $\mu\textrm{m}$. Excellent P-E hysteresis curves were achieved without pores or any defects between interlayers. As the thickness increased , the (111) preferred orientation disappeared from 1$\mu\textrm{m}$ to 3 $\mu\textrm{m}$ region, and the orientation of films became random above 3 $\mu\textrm{m}$. Dielectric constants and longitudinal piezoelectric coefficient d$\_$33/, measured by pneumatic method were saturated around the value of about 1400 and 300 pC/N respectively above the thickness of 0.8 7m. A micromachined piezoelectric cantilever have been fabricated using 0.8 $\mu\textrm{m}$ thickness PZT (52/48) films. PZT films were prepared on Si/SiN$\_$x/SiO$_2$/Ta/Pt substrate and fabricated unimorph cantilever consist of a 0.8 fm thick PZT layer on a SiNx elastic supporting layer, which becomes vibration when ac voltage is applied to the piezoelectric layer. The dielectric constant (at 100 kHz) and remanent polarization of PZT films were 1050 and 25 ${\mu}$C/$\textrm{cm}^2$, respectively. Electromechanical characteristics of the micromachined PZT cantilever in air with 200-600 $\mu\textrm{m}$ lengths are discussed in this presentation.