내부 확산법으로 제조한 $Nb_{3}$ Sn초전도선의 세선화에 의한 유연성 조사

Effect of wire diameters on superconducting and mechanical properties of internal tin processed $Nb_{3}$ Sn wires

Internal tin processed Nb$_3$Sn wires of intermediated worked state of were took from Mitsubishi and fabricated with various diameters ranging from 0.76 mm to 0.2 mm. These specimens were heat-treated at $460^{\circ}C$ for 70 h and at $570^{\circ}C$ for 100h to form bronze and at $700^{\circ}C$ for 100h to form Nb$_3$Sn compound. Bending strain Ic s of the wires were measured with various bending diameters ranging from flat to 76 mm. In order to investigate the sensitivity for strain, small diameters of wires were strain Ic at 6 T, 4.2 K. There were no breakage decrease during cold working to 0.2 mm of diameter and no decrease Jc to the diameter of 0.3 mm. The values of bending strain Ic of 0.2 mm and 0.3 mm diameters of the wires were not decreased at 76 mm of bending diameter.