초록
(Ba$\sub$0.6-x/Sr$\sub$0.4/Ca$\sub$x/)TiO$_3$(x=0.10, 0.15, 0.20) specimens were fabricated by the solid state reaction method and then the structural and dielectric properties as a function of the composition ratio and sintering temperature were studied. The BSCT(50/40/10) specimen sintered at 1500$^{\circ}C$ showed the highest average grain size(18.25 ${\mu}$m). The Curie temperature and dielectric constant at room temperature decreased with increasing Ca content. The dielectric constant and dielectric loss of the BSCT(50/40/10) specimen, sintered at 1450$^{\circ}C$, were about 4324 and 0.972% at 1KHz, respectively. Dielectric constant at room temperature decreased with increasing an applied field, tunability of the BSCT(50/40/10) sintered at 1300$^{\circ}C$ was 18%.