Abstract
Boron Phosphide films were deposited on the glass substrate at the low temperature, 55$0^{\circ}C$, by the reaction of B$_2$H$_{6}$ with PH$_3$ using CVD. $N_2$ was employed as carrier gas. The optimal gas rates were 50 $m\ell$/min for B$_2$H$_{6}$, 50 $m\ell$/min for PH$_3$ $m\ell$/min and 1.5 $\ell$/min for $N_2$. To investigate the annealing effect, the films were annealed for 1hour, 3hours in $N_2$ambient at 55$0^{\circ}C$ and tested. The deposition rate was 1000$\AA$/min and the refractive index of film was 2.6. The measurement of X-RD shows that the films have the preferred orientation of (1 0 1) and the intensity of the peak for (1 0 1) orientation decreases according to the annealing time. The data of VIS spectrophotometer proved that the films are transparent in the visible range and the maximal transmittance increases according to the annealing time; 75.49% for as-deposited, 76.71% for 1hr-annealed and 86.4 % for 3hrs-annealed. The measurement of AFM shows that the average surface roughness increases according to the annealing time; 73$\AA$ for as-deposited, 88.9$\AA$ for 1hr-annealed and 220$\AA$ for 3hrs-annealed. Also, The data of the secondary electron emission rate(Υ) shows that the secondary electron emission rate increases according to the annealing time; 0.317 for 1hr-deposited, 0.357 for 1hr-annealed and 0.537 for 3hrs-annealed. And, The measurement of FT-IR that the characteristic of transmittance in the infrared range was stabilized through annealing.ing.