Preparation of YBCO Superconducting Wire by Electrophoresis

전기영동법에 의한 YBCO 초전도 선재 제조 (I)

In this paper, by using the electrophoresis, preparation of YBCO superconducting wire deposited on metal Ag base wire was studied with its Properties. YBCO Powder could be prepared by solid state reactions with calcining and sintering processes. Superconducting wire prepared on metal Ag wire used as cathode of deposition base could be also fabricated in the YBCO/acetone-dispersed solution to obtain several tens of re thick films. And then it could be used as superconducting wire for measurement after calcination, sintering and oxygen absorption processes. In the process of film deposition, a catalyst I$_2$added into the suspension solution was very useful for preparing thick film of YBCO, and BaF$_2$ of additive material was also necessary for preparing crack-free wire of YBCO superconductor. As a result, YBCO superconducting wire added 2~3wt.% of BaF$_2$\ulcorner with catalyst, 12 had better deposition condition for uniform and dense YBCO wires, and critical current density, Jc was calculated at the value of 1,458A/$\textrm{cm}^2$(more than 10$^{3}$A/$\textrm{cm}^2$ ,77K, o[T]) of 30${\mu}{\textrm}{m}$ thick sample by 4 point prove method.