정전위법에 의한 Alloy 600의 입계응력부식균열 거동 연구

IGSCC(Intergranular stress corrosion cracking) behaviors of Alloy 600 were studied by the electrchemical ten methods of controlling specimens electrode potentials in the active-passive transition region of anodic polarization curve. Anodic polarization and static potential tests of stressed C-ring type MA Alloy 600 were carried out in 10% NaOH at 300 $^{\circ}C$ for 7days. It was confirmed that IGSCC of Alloy 600 was accellerated by maintaining the specimen potential in the susceptible active-passive transition region of anodic polarization curve. An intergranular crack was initiated on the surface area of C-ring specimens where protective oxide layer was broken down. And the depth of the crack growth was about 100 ${\mu}$m during the testing periods.