Abstract
The GaP crystals are growth by Synthesis Solute Diffusion(SSD) method and its properties are investigated. Etch pits density along vertical direction of ingot is increased from 3.8${\times}$10$^4$cm$\^$-2/ of first freeze to 2.3${\times}$10$\^$5/cm$\^$-2/ of last freeze part. The carrier concentration and mobilities are measured to 197.49$\textrm{cm}^2$/V. sec and 6.75${\times}$10$\^$15/cm$\^$-3/ at room temperature. The temperature dependence of optical energy gap is empilically fitted to E$\_$g/(T)=2.3383-(6.082${\times}$10$\^$-4/T${\times}$/(373.096+T)[eV]. Photo-luminescence spectra measured at low temperature are consist with sharp line-spectra near band-gap energy and radiative recombination between shallow Si-donor to Zn-acceptor and its phonon reprica, and broad emission. The infrared absorption in GaP is cause to phonon coupling modes of TO, LO, LA, TA$_1$, TA$_2$and vibration modes of Ga$_2$O, Si-donor and Zn-acceptor, respectively.