• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.263-266
• /
• 2003

The fine $YBa_2Cu_3O_x$ powder ($0.2{\sim}1.0\;{\mu}m$) is produced by sol-gel method, and electrophoresis deposition is used for the preparation of $YBa_2Cu_3O_x$ thick films which are deposited on Ag wire. The oriented $YBa_2Cu_3O_x$ was tried to be prepared by the zone-melting method under low oxygen partial pressure. The orientation and the phase composition were examined by the X-ray diffraction and the superconductivities were measured by 4 line method. The critical current densities are still quite low, which may be due to unsuitable technical parameters for zone-melting of $YBa_2Cu_3O_x$ thick films. Therefore the heat treatment condition and controlling of low oxygen partial pressure should be improved in the future experiment.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.6
• /
• pp.585-589
• /
• 2009

Extruder is divided to greatly three part at extrusion process. First, by hopper(Hopper) second, barrel(Barrel) with Screw that is point of extruder and third that is raw material supply wealth extrusion into dies(DIES) Part that decide shape of do product greatly divide. Hopper is role that distribute in raw material supply wealth (Feeding zone) of Screw preserving raw material in state of high quality how at extrusion process, and make distributed raw material as Screw in barrel rotates and 3 stage and inflicting heat and pressure raw material melting(Melting) state. And raw material of melting state Screw's measuring stoker(Metering zone) whereabouts anaphora do and product is completed through pipe channel of dies. Dies that is the most important as Screw in extrusion is part that is last part of melting state process of raw material and causes huge effect in quality of product. If more than design of dies happens, manufacture itself of dies is hard, but there are a lot of amount of losses accordingly. In this research, make pipe channel that raw material of melting state flows in dies can present dies basic design method through flow analysis of ideal pipe channel using CFdesign.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.366-369
• /
• 2003

High T$_{c}$ superconducting lines will be applied as key materials in the areas of power transmission line; magnetic levitation of vehicle; magnetic separation; magnetic energy storage and marine propulsion. A combination method of electrophoresis deposition and zone-melting for preparation of YBaCuO tape is proposed. The submicron particle powder of YBaCuO made by sol-gel method is used in the electrophoresis process. A 40~50${\mu}{\textrm}{m}$ thickness of YBaCuO film on Ag plate could be deposited in about three minutes. After deposition the film is rolled and heat treated in order to increase the density and the adhesion of the film to the Ag plate. Silver(Ag) and lead oxide(PbO) were added in the YBaCuO powder in order to reduce its melting point. The YBaCuO coating with controlled Ag and PbO contents was preliminarily zone-melted at about 945$^{\circ}C$.>.

• Journal of information and communication convergence engineering
• /
• v.1 no.2
• /
• pp.63-66
• /
• 2003

High $T_c$ superconducting lines will be applied as key materials in the areas of power transmission line; magnetic levitation of vehicle; magnetic separation; magnetic energy storage and marine propulsion. A combination method of electrophoresis deposition and zone-melting for preparation of YBaCuO tape is proposed. The submicron particle powder of YBaCuO made by sol-gel method is used in the electrophoresis process. A 40∼50 ${\mu}\textrm{m}$ thickness of YBaCuO film on Ag plate could be deposited in about three minutes. After deposition the film is rolled and heat treated in order to increase the density and the adhesion of the film to the Ag plate. Silver(Ag) and lead oxide(PbO) were added in the YBaCuO powder in order to reduce its melting point. The YBaCuO coating with controlled Ag and PbO contents was preliminarily zone-melted at about $945^{\circ}C$.

• Korean Journal of Crystallography
• /
• v.3 no.2
• /
• pp.85-97
• /
• 1992

EBFZM( Electron Beam Floating Zone Melting) 법을 이용하여 몰리브덴에서의 금속계 불순물과 침입형 불순물의 정련기구 및 단결정 성장기구를 연구하 였다. Fe, Cr, Co등의 금속계 불순물은 몰리브덴과의 평형증기압의 차이에 따른 불순물의 선택적 증발에 의하여 우수한 정련효과를 나타내며, 몰리브덴보다 응점이 높은 Ta, W는 잘 제거되지 않았다. 한편 대역 정제에 의한 정련효과는 미약함을 확인하였다. EBF ZM은 C,0,N등의 침입형 불순물의 정련에도 효과적 이었다. 본 연구의 모든 조건에서 몰리브덴은 단결정으로 성장하였으며 2차 재결정 epitaxy에 의한 단결 정 성장기구가 제시되었다. 몰리브덴 단결정 내의 전 위밀도는 strain-anneal법에 의한 단결정의 경우보다 높았으며,본 실험의 열처리 조건에서는 변화하지 않았다. The purification and single crystal growth mechanisms of molybdenum were analysed in EBFZM ( electron beam floating zone melting). Metallic impurities of Fe, Cr, Co were purified efficiently but Ta and W were not removed well in this study. It was due to a preferential evaporation of the elements caused by the difference in equillibrium vapor pressure between the elements and molybdenum. The pu- rification effect by zone refining was not significant. The EBFZM also refined the interstitial impurities of C, 0 and N, effectively. The single crystals of molybdenum were grown regardless of the experimental conditions and the secondary recrystallization epitaxy was surge sled as a growth mechanism. The dislocation density in single crystal was higher than that by strain-anneal method, and was not reduced by heat treatments.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.528-535
• /
• 1997

$LiTaO_3$ single crystals of congruently melting composition were grown by the halogen lamp type floating zone system. Calcination and sintering parameters for the growth were established. Optimum crystal growth conditions were investigated by a controlling of growth rates, rotation speeds and atmospheres. Based on the melting aspect and the shape of molten zone, stable conditions could not be found in air or Na atmosphere. However the growth stability in Ar atmosphere was more regular than that in air or $N_2$. The grown crystals were characterized using Laue back reflection, Curie temperature, refractive index and transmittance. Curie temperature fluctuation in the section of the grown crystal part of top, body and tail was $1^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.91-94
• /
• 2002

The conditions of zone-melting method such as a sample travel speed in a furnace, content of Nd422, control of melting temperature, and heat-treatment with/without Ar gas for $NdBa_{2}Cu_{3}O_{7-\delta}$ superconductor was optimized, As a results, a $NdBa_{2}Cu_{3}O_{7-\delta}$ sample with a surface area of $25mm^{2}$ showed a good superconducting properties when its travel speed was 6 mm/h, The improvement of superconductivity added with 10~20 wt% of Nd422 phase increasing pinning effect was also shown. The critical current density, $J_{c}$ was remarkable affected by the condition of heat-treatment temperature of $NdBa_{2}Cu_{3}O_{7-\delta}$superconductor with/without Ar ambient gas.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05b
• /
• pp.12-15
• /
• 2003

The YBaCuO thick film was deposited by the electrophoresis in the solution with different dimension particles. The morphology of the films deposited from different particles size was compared. The powder made by sol-gel method has the submicron particles, which deposit the most smooth film, and without microcracks after sintering. After sintering of the deposited film, the zone-melting process was carried out in low oxygen partial pressure (100 Pa) and Ag was used as substrate. And the zone-melted YBaCuO was studied by XRD.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.2
• /
• pp.68-72
• /
• 2004

Sm-doped YBCO high $T_c$ superconductor was directionally grown by zone melt growth process in air atmosphere. Cylindrical green rods of $(Sm/Y)_{1.8}Ba_{2.4}Cu_{3.4}O_{7-x}$[(Sm/Y)1.8] oxides were fabricated by cold isostatic pressing (CIP) method using rubber mold. Based on the variation of melting temperature and growth rate, the microstructure and superconducting properties were systematically measured by using optical micrographs, TEM and SQUID magnetometer. In this study optimum melting temperature and growth rate were $1085^{\circ}C$ and 3.5 mm/hr respectively. Nonsuperconducting $(Sm/Y)_2BaCuO_5$ inclusions of (Sm/Y)1.8 superconductor were uniformly distributed within the superconducting (Sm/Y) $Ba_2Cu_3O^{7-x}$ matrix. The directionally melt-textured (Sm/Y)1.8 superconductor showed an onset $T_c$ $\geq$ 90K and sharp superconducting transition.