• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1992년도 춘계학술대회 논문집
• /
• pp.18-22
• /
• 1992

This paper presents the process of manufacturing technology of ceramics ferrule for optical fiber connector. Precision zirconia ceramic ferrules is widely used for high performance and low cost single mode optical fiber connectors. To polish the hole of the zirconia ceramic ferrule, the wire lapping instrument is developed and the machining experiment is conducted. Through the centerless grinding using diamond wheel the surface roughness of zirconia ceramics ferrule is below the 1 .mu. m Rmax.

• 한국정밀공학회지
• /
• 제9권3호
• /
• pp.67-72
• /
• 1992

This paper presents the process of manufacturing technology of ceramics ferrule for opitcal fiber connector. Precision zirconia ceramic ferrules is widely for high performance and low cost single mode optical fiber connectors. To polish the hole of the zirconia ceramic ferrule, the wire lapping instrument is developed and the machining experiment is conducted. Through the centerless grinding using diamond wheel the surface roughness of zirconia ceramics ferrule is below the 1$\mu$m Rmax.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.1092-1098
• /
• 2004

Today the demand of the optical communication components has been increased. Zirconia Ferrule has become the one of the most important elements because it determines transmission efficiency and quality of information in the optical communication system. Grinding is the major process in the ferrule manufacturing process which require high processing precision. In this reseach, specially designed spindle, chucking system, loading & unloading system and cooling system, as a supporting experimental equipment for development of an Intelligent Coaxial Grinding System (ICGS) for Zirconia Ferrule processing, is developed. We are also analized the adaptability of ICGS in practical use, through the way of evaluation for the performance of the each systems above.

• 한국결정성장학회지
• /
• 제13권4호
• /
• pp.162-167
• /
• 2003

광페롤용 안정화 지르코니아 소결체의 특성을 평가하기 위하여, A, B와 C사의 원료를 이용하여 1350, 1400 및 $1450^{\circ}C$로 소결하여 시편을 제작하였다. 각각의 열처리 온도에 따른 결정화도, 미세구조 및 기계적 특성을 조사하였다. X-선 회절 분석법과 전계방사 주사형 전자현미경을 이용하여 소결된 시편의 결정화도와 미세구조를 분석하였으며, 만능재료 시험기와 비이커스 경도계를 이용하여 꺽임 강도와 비이커스 경도를 측정하였다 실용적인 측면에서 볼 때, 비교적 저온인 $1350^{\circ}C$로 소결한 시편 B의 경우가 tetragonality도 높고 좋은 기계적인 강도를 나타냈다.

• 한국재료학회지
• /
• 제20권11호
• /
• pp.570-574
• /
• 2010

A diamond-like carbon (DLC) film deposited on a WC disk was investigated to improve disk wear resistance for injection molding of zirconia optical ferrule. The deposition of DLC films was performed using the filtered vacuum arc ion plating (FV-AIP) system with a graphite target. The coating processing was controlled with different deposition times and the other conditions for coating, such as input power, working pressure, substrate temperature, gas flow, and bias voltage, were fixed. The coating layers of DLC were characterized using FE-SEM, AFM, and Raman spectrometry; the mechanical properties were investigated with a scratch tester and a nano-indenter. The friction coefficient of the DLC coated on the WC was obtained using a pin-on-disk, according to the ASTM G163-99. The thickness of DLC films coated for 20 min. and 60 min. was about 750 nm and 300 nm, respectively. The surface roughness of DLC films coated for 60 min. was 5.9 nm. The Raman spectrum revealed that the G peak of DLC film was composed of $sp^3$ amorphous carbon bonds. The critical load (Lc) of DLC film obtained with the scratch tester was 14.6 N. The hardness and elastic modulus of DLC measured with the nano-indenter were 36.9 GPa and 585.5 GPa, respectively. The friction coefficient of DLC coated on WC decreased from 0.2 to 0.01. The wear property of DLC coated on WC was enhanced by a factor of 20.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1993년도 춘계학술대회 논문집
• /
• pp.6-10
• /
• 1993

빛을 통신매체로 사용한 광통신은 저손실, 광대역성, 대용량화등의 장점 때문에 많은 중장거리 통신을 점유하고 있으며, 대형가입자군을 위한 광가입자망이나 LAN등에도 시험적용되고 있다. 따라서 광통신에 있어 광FIBER를 연결시키는 CERAMIC단자를 연구개발하는데 그목적을 두었으며, CERAMIC 단자의 재질로서는 구조재료로 주로 사용되는 ZIRCONIA(psz)를 선정하였으며 또한 정밀성형 및 소결등을 검토하였다.