• 한국분말재료학회지
• /
• 제10권3호
• /
• pp.201-208
• /
• 2003

Distributions of diamond particles protruding on the surface of worn diamond segments in circular saw has been investigated. Scanning electron microscope was used to examine the worn ,surface and radial saw blade wear and grinding ratio was measured. The number of protruded diamond particle was approximately 50% of the total number of particles, and that was independent of diamond particle concentration and table speed. It was also noted that the inter-particle distance did not follow a symmetric function like Gaussian distribution function, instead it fitted well with a probability density function based on gamma function. The distribution of inter-particle spacing, therefore, was analyzed using a gamma function model.

• 소성∙가공
• /
• 제19권6호
• /
• pp.357-362
• /
• 2010

Dry sliding wear behavior of pure Fe and Cu which have BCC and FCC crystal structure, respectively, was investigated. The wear characteristics of the pure metals with different crystal structure were compared. Dry sliding wear tests were carried out using a pin-on-disk wear tester at various loads under the constant sliding speed condition of 0.15 m/s against a silica ball at room temperature. Sliding distance was fixed as 600 m for all wear tests. Wear rate of a specimen was calculated by dividing the weight loss of the specimen after the test by the specific gravity and sliding distance. Worn surfaces and wear debris were analyzed by SEM. The wear of both pure Fe and Cu proceeded with surface deformation, resulting in similar wear rates despite of their structure difference under the current test conditions. Wear rates of both metals were low if the surface deformation due to wear forms thick surface-deformation layer that is strain hardened beneath the wearing surface. The pure Cu specimens showed a lot of oxides on the worn surface when tested at low loads less than 5 N, which resulted in very low wear rate.

• Tribology and Lubricants
• /
• 제22권3호
• /
• pp.144-148
• /
• 2006

The experimental investigation was performed to find the associated changes in characteristics of fretting wear with various water temperatures. The fretting wear tests were carried out using the zirconium alloy tubes and the grids with increasing the water temperature. The tube materials in water of $20^{\circ}C,\;50^{\circ}C\;and\;80^{\circ}C$ were tested with the applied load of 20 N and the relative amplitude of $200{\mu}m$. The worn surfaces were observed by SEM, EDX analysis and 2D surface profiler. As the water temperature increased, the wear volume was decreased, but oxide layer was increased on the worn surface. The abrasive wear mechanism was observed at water temperature of $20^{\circ}C$ and adhesive wear mechanism occurred at water temperature of $50^{\circ}C,\;80^{\circ}C$. As the water temperature increased, surface micro-hardness was decreased, but wear depth and wear width were decreased due to increasing stick phenomenon. Stick regime occurred due to the formation of oxide layer on the worn surface with increasing water temperatures

• KSTLE International Journal
• /
• 제2권2호
• /
• pp.138-141
• /
• 2001

Tribological behaviors of a borate of triethanolamine in water solution were evaluated using a four-ball wear tester. X-ray photoelectron spectroscopy (XPS) was employed to study tribochemical species on worn scars of steel balls. Results show that a thick deposit layer was produced on the worn scars, which came from the decomposition of the borate. The surface film on the worn scars was mostly consisted with H$_3$BO$_3$, B$_2$O$_3$and large amounts of ferricyanides.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제34회 추계학술대회 개최
• /
• pp.374-379
• /
• 2001

Tribochmical behaviors of a borate of triethanolamine in water solution were evaluated using a four-ball wear tester. X-ray photoelectron spectroscopy (XPS) was employed to study tribochemical species on worn scars of steel balls. Results show that a thick deposit layer was produced on the worn scars, which came from the decomposition of the borate. The surface film on the worn scars was mostly consisted with H$_{3}$BO$_{3}$, B$_{2}$O$_{3}$ and large amounts of ferricyanides.

• KSTLE International Journal
• /
• 제6권2호
• /
• pp.39-44
• /
• 2005

Friction and wear properties of the Boron carbide ($B_{4}C$) coating 100 nm thickness were studied under various relative humidity (RH). The boron carbide film was deposited on silicon substrate by DC magnetron sputtering method using $B_{4}C$ target with a mixture of Ar and methane ($CH_4$) as precursor gas. Friction tests were performed using a reciprocation type friction tester at ambient environment. Steel balls of 3 mm in diameter were used as counter-specimen. The results indicated that relative humidity strongly affected the tribological properties of boron carbide coating. Friction coefficient decreased from 0.42 to 0.09 as the relative humidity increased from $5\%$ to $85\%$. Confocal microscopy was used to observe worn surfaces of the coating and wear scars on steel balls after the tests. It showed that both the coating surface and the ball were significantly worn-out even though boron carbide is much harder than the steel. Moreover, at low humidity ($5\%$) the boron carbide showed poor wear resistance which resulted in the complete removal of coating layer, whereas at the medium and high humidity conditions, it was not. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) analyses were performed to characterize the chemical composition of the worn surfaces. We suggest that tribochemical reactions occurred during sliding in moisture air to form boric acid on the worn surface of the coating. The boric acid and the tribochemcal layer that formed on steel ball resulted in low friction and wear of boron carbide coating.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2002년도 춘계학술대회 논문집
• /
• pp.844-847
• /
• 2002

This paper is to investigate the wear behavior of submerged-arc clad materials by the wear test with a ball-on-disk type wear testing machine in air. The specimens were clad with Stoody105 alloy wire on a carbon steel (SM45C) substrate by submerged-arc cladding process under different welding parameters. The wear behavior of the cladding through ball-en-disk test has been studied under the wear load from 5N to 16N and sliding speed from 8cm/s to 35cm/s. The weight of the specimen loss was measured. Scanning electron micrographs of the worn surface show a layer of oxide film formed on the worn surface. Oxidation wear mechanism controls the wear process. The spalling of the oxide is caused by the repeated rubbing fatigue mechanism.

• 한국정밀공학회지
• /
• 제20권1호
• /
• pp.179-186
• /
• 2003

This paper is to investigate the wear behavior of submerged-arc claddings by the wear test with a ball-on-disk type wear testing machine in air. The specimens were clad with Stoody105 alloy wire on a medium carbon steel (SM45C) substrate by submerged-arc cladding process under different welding parameters. The wear behavior of the cladding through ball-on-disk test has been studied under the wear load from 5 to 16 N and the sliding speed from 8 to 35 cm/s. The weight loss of the specimen was measured. Scanning electron micrographs of the worn surface show a layer of oxide film formed on the worn surface. Oxidation wear mechanism controls the wear process. The spatting of the oxide is caused by the repeated rubbing fatigue mechanism.

• 대한기계학회논문집
• /
• 제19권9호
• /
• pp.2122-2132
• /
• 1995

There are some cases which require to grasp the abrasion resistance property in the fields of the high-technology to be required the high specific strength and modulus. In this study, wear test with the various test temperature and velocity were performed in the SiCw/A16061 composite and A16061 matrix using the wear test machine of the ring-on-disc type. As the results, the friction and wear properties by various test temperature and velocity were examined. The worn surface has observed by scanning electron microscope in order to examine the wear mechanism.

• Journal of Welding and Joining
• /
• 제19권5호
• /
• pp.540-547
• /
• 2001

This study has evaluated the wear behavior of PTA (Plasma Transferred Arc) Inconel 625 and Stellite 6 overlays on Nimonic 80A substrate. Nimonic 80A alloy was also included for comparison. In order to evaluate the wear performance, three-body abrasive wear test and pin-on-disk dry sliding wear test were performed. Microstructural development during the solidification of deposits is also discussed. Wear test results show that the wear rate of Stellite 6 deposit is lower than that of Inconel 625 deposit and Nimonic 80A. The sliding wear resistance of overlay deposits follows a similar trend to the abrasive wear resistance, but for Nimonic 80A. The main wear mechanisms were abrasive wear for Inconel 625 deposit, adhesive wear and delamination for Stellite 6 deposit in pin-on-disk dry sliding wear test and ploughing in three-body abrasive wear test. Cross sectional examinations of the worn surface of pin specimens after pin-on-disk dry sliding wear test implies that the plastic deformation near worn surface has occurred during the wear testing.