• Journal of the Korean Wood Science and Technology
• /
• v.31 no.5
• /
• pp.80-87
• /
• 2003

This research was carried out to examine physical and mechanical properties of clay-woodceramics which were carbonized for 3 hours in a special furnace from 3 layers-clay-woodparticleboard made from pallet waste wood, phenol formaldehyde resin(hereafter PF, Non volatile content 52%, resin content 30%) and clay(10%, 20% and 30%). Carbonization temperature was 400℃, 600℃ and 800℃. The results are summarized as follows: 1. The higher the carbonization temperature, the higher the dimensional shrinkage and the lower the carbonization yield ratio. But the higher the clay addition, the lower the dimensional shrinkage and the higher carbonization yield ratio. 2. The higher the carbonization temperature, the higher the water absorption and the density. The higher the clay content, the higher the density. 3. The higher the carbonization temperature, the higher the bending Modulus of Rupture and bending Modulus of Elasticity.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.4
• /
• pp.9-13
• /
• 2007

Using sawdust boards made of pine by differing the percentage of resin impregnation, wood-ceramics were manufactured by carbonizing temperature at $650^{\circ}C$. Their electrical properties and surface temperature were measured by sending an electric current. As electrical resistance of woodceramic was lower, its surface temperature, even in a low voltage, became higher. It seemed to be necessary to applying higher voltage to the woodceramic to raise the surface temperature by target temperature $70^{\circ}C$ or more in this study, according as resistance increased. When the voltage increased, woodceramics showed higher level all in electric current, electric power and surface temperature. Arrival time, electric current and electric power increased with increase of target temperature under constant voltage.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.2
• /
• pp.105-110
• /
• 2013

A repeated impregnation and carbonization process was performed to prepare high-density woodceramics using MDF. The physical properties were estimated to further confirm morphologically structurally occurred changes of one-time and two-time phenolic resin treated and carbonized woodceramics. As compare one-time and two-time carbonized woodceramics, the increasing rate of weight and density declined after second carbonization as the resin impregnation ratio grew higher, and when the resin impregnation ratio was 40 percent, the weight and density of the second carbonization increased more than in the first step by 20.5% and 33.9% respectively which were the highest rates.

• Journal of the Korea Furniture Society
• /
• v.17 no.1
• /
• pp.23-32
• /
• 2006

This study was carried out to explore a new application of traditional Hanji and obtain fundamental properties for producing Hanji wallpaper by incorporating ceramics from wood and rice-husk as an interior building material. The results of properties determined were summarized as follows: The addition of ceramics in Hanji paper reduced its apparent density, but increased bulk density due to the ceramic particles distributed on the surface and inside the fiber of Hanji wallpapers. In particular, woodceramic particles were specifically distributed on the fiber surface, while particles of rice-husk ceramics were permeated into the inside surface of fibers. The density of rice-husk ceramics were greater than that of woodceramics. The physical properties of Hanji wallpapers, such as breaking strength, wet breaking strength, burst strength, tear index and folding endurance were deteriorated with the addition of ceramics. However, the addition of woodceramics in the Hanji wallpaper resulted in better strength in most cases than that of rice-husk ceramics, except tear strength. Therefore, an optimum addition level of woodceramics into the wallpaper was found to be 5% on the basis of intensity. The addition of ceramics also prolonged the combustion time because it lowered air permeability and brightness of the wallpaper.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.6
• /
• pp.83-88
• /
• 2003

The woodceramics are porous amorphous carbon and glassy carbon composite materials. Woodceramics attracted a lot of attention in recent years because they are environmentally friendly and because of their unique functional characteristics such as catalysis, moisture absorption, deodorization, purification, carrier for microbial activity, specific stiffness, corrosion and friction resistance, and their electromagnetic shielding capacity. In this paper, we made new products of clay-woodceramics to investigate the industrial analysis and ethylene gas adsorption for basic data of building- and packging- materials keeping fruit fresh for a long time. Clay-woodceramics were carbonized for 3 h of heating in a special furnace under a gas flow of nitrogen(15 ml/min.) from 3 layers-clay-woodparticleboard made from pallet waste wood, phenol- formaldehyde resin(hereafter PF, Non volatile content:52%, resin content 30%), and clay(10%, 20% and 30%). Carbonization temperature was 400℃, 600℃ and 800℃. Experimental results shows that the higher the carbonization temperature, the higher the fixed carbon and the lower the volatile contents. The higher the clay content, the more the ash content. The higher the carbonization temperature, the more the ethylene gas adsorption. Carbonization temperature of 800℃ gave the best reslts as same as that of white charcoal and activated carbon.(800℃-clay-woodceramic: 5.36 ppm, white charcoal: 5.66 ppm, activated carbon: 5.79 ppm) The clay contents did not make difference of ethylene gas adsoption.