• Journal of the Korea Furniture Society
• /
• v.17 no.1
• /
• pp.83-89
• /
• 2006

Because the surface of pine wood is very soft, there have been many attempts, like as surface coating, resin impregnation, and densificationt, to harden the surface of wood for its interior use. This study was carried out for surface hardening of pine wood by laminating of melamine resin sheet. The effect of laminating method on the characteristics of melamine resin sheet-laminated wood(MLW) was investigated. Flat-sawn softwoods were suitable for MLW making. And the pre-drying of wood at $105^{\circ}C$ for 30min, before laminating, was effective for preparing of defect-free MLW. The abrasion resistance of pine wood was greatly improved by laminating of melamine resin sheet on its surface. Consequently, the laminating of melamine resin sheet was proved to be a favorable method for improvement of surface abrasiveness of pine wood.

• Journal of the Korean Wood Science and Technology
• /
• v.26 no.1
• /
• pp.38-50
• /
• 1998

Laser cutting tests were conducted to investigate the laser cutting characteristics of solid woods such as 25mm-thick white oak(Quercus acutissima) and maple(Acer mono), and wood-based panels such as 15mm-thick medium density fiberboard and particleboard. Test variables were laser power, cutting speed, grain direction, and moisture content. Specific cutting energy was measured and the qualities of cut surface were estimated in constant laser power. Specific cutting energy of white oak was larger than that of maple, and specific cutting energy of medium density fiberboard was smaller than that of particleboard. For both white oak and maple, specific cutting energy of green wood was smaller than that of air-dried wood because weight loss of moisture evaporation in green wood was larger than that in air-dried wood. In laser-cut surface, wood cells were not deformed and damaged, but in circular saw-cut surface fibers were pushed out and cut, and wood cells were deformed severely. However, mechanical surface roughness of saw-cut surface was smoother than that of laser-cut surface because of the existence of undeformed cell cavity in laser-cut surface.

• Journal of the Korea Furniture Society
• /
• v.23 no.4
• /
• pp.460-466
• /
• 2012

This study was conducted to investigate the surface hardness of thermally-compressed larch wood by compression set and temperature. The surface hardness of thermally-compressed larch wood increased with increasing compression set and temperature. For compression set 60%, the specific gravity was increased as 0.93. However, the surface hardness was lower value as 31.1 N/$mm^2$ compared with a similar specific gravity of the tropical timber. For density profile, less than compression set 40%, compression was observed mainly surface area. On the other hand, more than 50%, density profile variation was reduced by compression of central part. Results of this study indicate that thermally-compressed larch wood can be replace some imported hardwoods such as oak or cherry. However, thermally-compressed larch wood was difficult to replace the tropical timber being imported in terms of surface hardness.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.3
• /
• pp.1-7
• /
• 2004

The application of abrasive-assisted high energy water-jet was investigated as a possible new method of cutting wood. In this study the maximum cutting speeds for species of various wood density were determined and water-jet machining characteristics were investigated for sixteen Korean domestic species. The maximum cutting speed ranged from 200 to 750 mm/min. The results indicate that wood density affects machining characteristics such as maximum cutting speed, surface roughness, and kerf width. Roughness of surface generated increased and kerf width decreased as penetration depth increased.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.4
• /
• pp.38-42
• /
• 1999

Average moisture content of 30mm-thick Korean red pine(Pinus densiflora) was estimated nondestructively and continuously using surface temperature rise by radiation heating and moisture gradient profile in wood. The surface temperature rises increased as surface moisture contents decreased and good relationships were found between surface moisture contents and surface temperature rises at three different feed speeds of 10, 20 and 30 m/min. Average moisture content could be described as a function of surface moisture content and wood thickness.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.1
• /
• pp.82-92
• /
• 2021

Nakdong technique is an unfamiliar scorching treatment using an iron heated in a kiln over 1000℃. It is a typical convention in Asian countries to treat Nakdong on the surface of paulownia species. The scorching treatment changes the surface characteristics as well as the color of the wood. This study focused on the effects of functional features such as water resistance, anti-mold, anti-termite, and sound improvement because this treatment is usually used on paulownia wood-bodied musical instruments surface. It took 28'57" for Nakdong-iron treated surface to absorb a droplet of water. The absorbance time of iron treated surface was longer than that of torch treated one. There was no noticeable effect on the anti-mold test. On the anti-termite test, there was nearly 3% more mean mass loss on the torch samples than controlled and iron treated ones. In examining the sound radiation coefficient before and after Nakdong treatment, the Nakdong-iron treated surface showed an increase in the average value of 1.2 m4/kg s, which means that it has sound quality improvement. Through this research, the Nakdong technique results are expected to be used as basic-data for further research and give a practical idea for using the traditional treatment method on the wood surface.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.3
• /
• pp.274-282
• /
• 2021

Transparent and colorless melamine-urea-formaldehyde (MUF) resins make it difficult to identify the area of wood failure percentage (WFP) in the fracture surface of bonded wood specimens. Therefore, in this study, we develop a method of measuring WFP after the adhesion strength measurement of MUF resins under shear stress. The fractured wood surface of b lock shear strength (BSS) specimens bonded with cold-setting MUF resins at three melamine contents (20%, 30%, and 40%) was marked black, and then, WFP was accurately measured via image analysis. WFP values measured using this method consistently increased with BSS as the melamine content increased, showing the reliability of this new method. The results suggested that this new method is useful and reliable for measuring the WFP of the fracture surface of wood specimens bonded with colorless adhesives such as urea-formaldehyde, MUF, and melamine-formaldehyde resins.

• Journal of the Korean Wood Science and Technology
• /
• v.23 no.1
• /
• pp.54-60
• /
• 1995

This paper reports on the changes of equilibrium moisture contents and specific surface areas of Poplar wood(Populus euramericana) for various steam explosion treatments. Equilibrium moisture contents(EMC) and specific surfaces of steam exploded woods were measured under the moisture adsorption course at 25$^{\circ}C$, and compared with those of other materials and wood meals. The EMCs of steam exploded wood meal were 1~5% less in comparison with that of wood meal. In the case of delignified steam exploded wood meal and delignified wood meal, the same tendency was appeared too. But absolute values of EMCs for delignified wood meals were larger than those of the wood meal. For the changes of EMC by the steam exploded conditions, the EMC decreased with the increase of the steam explosion pressure. On the other hand, specific surface areas were calculated from BET plots based on amounts of monomolecular vapor adsorption of various wood meals. Specific surface areas of the wood meal and delignified wood meal were 90~145, 34~90($m^2/g$) respectively, and which were greater in comparison with those of steam exploded wood meals and delignified steam exploded wood meals. From these results, it is considered that the amount of water vapor adsorption was decreased by the increase of the crystallinity, effect of heat treatment, and coating by melted lignin in during the steam explosion.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.4
• /
• pp.600-606
• /
• 2016

Wood-based composite panels such as plywood, particleboard (PB), or medium density fiberboard (MDF) are mostly used in the lamination on their surface for the manufacturing of furniture, or interior building products, the concern on the formaldehyde emission (FE) from the surface laminated wood panels is increasingly attracting attentions from the public. Thus, this study was conducted to understand influence of surface laminating materials to the FE from PB and MDF with or without edge sealing, using 24-hour desiccator method. Both PB samples that had been laminated on their surface with low-pressure laminate (LPL) or polypropylene (PP) film and MDF that had been treated with poly(vinyl chloride) (PVC) or coating were tested for the FE with or without edge sealing. As expected, the FE of PB with the sealed edges decreased to 37.4% and 80.7% with the LPL and PP lamination, respectively. The surface laminated MDF with the sealed edges also showed a decrease in the emission up to 57.8% and 54.3%, with the PVC lamination and coating, respectively. However, the coated MDF samples showed 5.3% increase in the emission when their edges were not sealed, indicating a FE form the solvent used for coating. These results showed that the type of surface lamination materials on wood-based composite panels has a great impact on their resultant FE, indicating that the influence of surface laminating materials should be taken into consideration for the formaldehyde mission measurement.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.1
• /
• pp.53-59
• /
• 2007

The cutting tests of wood patterns are carried out using CNC milling machine. The cutting forces are monitored to analyse the cutting process. The surface characteristics of machined surface are investigated at various cutting conditions such as cutting speed, feed speed, cutting direction of wood pattern and wood material. In the CNC end-milling, the surface roughness increases as feed speed increases and decreases as cutting speed increases. However, the cutting force and surface roughness are different along the cutting direction and material of wood pattern.