• Journal of the Korean Wood Science and Technology
• /
• v.39 no.1
• /
• pp.86-94
• /
• 2011

Pyrolytic lignin was obtained from biooil produced with yellow poplar wood. Fast pyrolysis was performed under various temperature ranges and residence times using fluidized bed type reactor. Several analytical methods were adopted to characterize the structure of pyrolytic lignin as well as the effect of pyrolysis temperature and residence time on the modification of the lignin. The yield of pyrolytic lignin increased as increasing pyrolysis temperature and decreasing residence time of pyrolysis products. The molecular weight of pyrolytic lignin determined by gel permeation chromatography (GPC) was approximately 1,200 mol/g, which was approximately a tenth of milled wood lignin (MWL) purified from the same woody biomass. Based on analytical data, demethoxylation and side chain cleavage reaction were dominantly occurred during fast pyrolysis.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.6 s.134
• /
• pp.79-86
• /
• 2005

Aspen wood (Populus tremuloides, L.) was biotreated with Ceriporiopsis subvermispora for 1, 2, 4, and 6 weeks to observe the physical/chemical modification of wood components. Milled wood lignins (MWLs) isolated from each decayed wood were analyzed by gel permeation chromatography (GPC) and nitrobenzene oxidation (NBO). As fungal treatment was progressed, lignin contents continuously decreased up to 20% after 6-week treatment. The lignin polymer could be fragmented to low-molecular phenolics, which make an enhancement of alkali solubility. Holocellulose contents were not affected severely during the period of fungal treatment, only reduction of 5~6% compared to the control. Xylose contents were decreased gradually from 23.4% to 18% after 6 weeks, whereas alpha-cellulose remained almost unchanged. Gel permeation chromatography (GPC) indicates that molecular weight of lignin undergoes a slight decrement for 4 weeks of fungal treatment. Nitrobenzene oxidation revealed that total yield of NBO products of lignins were lowered ca 20% after fungal treatment. Sum of syringaldehyde and syringic acid are remarkably decreased. However, increment of sum of vanillin and vanillic acid was surprisingly observed. These results work as indirect evidence that a specific lignolytic reaction, maybe selective demethoxylaytion of S-lignin, can occur during fungal treatment of aspen wood by C. subvermispora.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.36 no.4 s.107
• /
• pp.41-48
• /
• 2004

To make a basepaper for multipurposed seed paper, old news print (ONP) and mixed office waste paper (MOW), modified and unmodified with a commercial cellulase, were investigated. Each handsheet was applied with different chemicals such as insecticides, germicides and herbicides. The interactions behaviors of chemicals used with base papers were evaluated by means of the contents of chemicals impregnation and dissolving behaviors in water and soil. The ONP and MOW treated with the cellulase had higher impregnation and dissolving capacities in both water and soil than untreated ONP and MOW. However, the modified ONP showed lower impregnation and dissolving capacities compared to the modified MOW. The content of impregnation of chemicals would be affected with the degree of microfibrils produced by the modification treatment. Otherwise, dissolving capacities of chemicals depend on the affinity of the residual lignin in the paper.

• Journal of the Korean Wood Science and Technology
• /
• v.24 no.4
• /
• pp.1-6
• /
• 1996

Extracts from bark have been studied with a view to producing water-proof wood adhesives. Lately many softwoods, such as radiata pine from New Zealand and larch from Siberia, Russia, have been imported and utilized, and their residual barks would be expecting as potential raw materials for something useful chemicals. The great effort toward utilization of bark extractives as a chemical feedstock has been made on a worldwide level. However few report has been done for the utilization of tree bark extractives in Korea. Hot-water extracts were prepared from barks of Japanese larch(Larix leptolepis). Siberian larch(Larix gmelinii) and Radiata pine(Pinus radiata). The effect of various factors, such as particle size, liquor ratio, extraction temperature, and reaction time, on the extractive yields was discussed. Particle sizes affected the hot-water extractives: the finer the particle size, the higher extractives and extract efficiency. Higher temperature and higher liquor ratio were more effective. Extractives from Japanese larch were relatively less than those from Siberian larch and Radiata pine barks. Formaldehyde precipitates was the highest in extractives of Radiata pine barks. It could be concluded that Siberian larch bark was the best raw material for tannin adhesives, because its extractive yield was higher than those of the other barks.

• Journal of the Korean Wood Science and Technology
• /
• v.50 no.1
• /
• pp.59-67
• /
• 2022

Dietary fiber is considered a feed ingredient with high nutritional value in the broiler feed industry. Pine chips contain a large amount of dietary fiber and require some modification for use as broiler feed. In this study, pine chips were subjected to steam explosion under different severity factor (Ro) conditions to improve the chemical and physical properties of dietary fiber. The highest water-holding capacity, oil-holding capacity, and swelling capacity were found for Ro 4.0, followed by Ro4.5 and 3.5. The optimal condition for the steam explosion was determined to be Ro 4.0 (reaction temperature of 210℃, and reaction time of 6.0 min). Under these conditions, the water-holding capacity, oil-holding capacity, and swelling capacity of steam-exploded pine chips were 8.3 g/g, 6.5 g/g, and 5.0 mL/g, respectively. This study may contribute to the application of lignocellulose and related products in the broiler feed industry.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.6
• /
• pp.498-504
• /
• 2011

The purpose of this study was to investigate and develop an eco-frendly wood adhesive based on vegetable oil (especially soybean oil), the renewable and sustainable natural resources, using ozonification technology for the chemical structure modification. The waste soybean oil (WSBO) was reacted with $O_3$ at the rate of $450m{\ell}$(acetone) : $50m{\ell}$ (WSBO) for different times, 1, 2, 3 hrs. The investigation of the modified chemical strecture of the ozonied WSBOs were conducted using FT-IR. As ozonification time increased, the peak of the unsaturated double bonds was disappeared especially ozonized-3hrs and aldehyde or carboxyl peak appeared because ozonification broke the oil into small molecules. The plywood were made at $150^{\circ}C$ with 4 minutes hot-press time using the different ozonized 3 hrs WSBO/pMDI adhesives and were tested for the dry, wet, cyclic boil test according to the Korea Industrial Standard F3101 Ordinary plywood. The bond strengths gradually increased until 1 : 0.5~1 : 3, but it decreased 1 : 4, as the contents of pMDI increased. The results of the dry, wet and cyclic bond strengths the equivalent ratio was formed approximately between 1 : 2~1 : 3. And the 1 : 1~1 : 4 strengths met constantly the standard requirement of 7.0kgf/$cm^2$ (KS F3101). From the comprehensive view on the results of above experiment, it could be confirmed that ozonized WSBO/pMDI has characteristics of effective reactivity and wet stability showed as an excellent candidate of wood adhesive applications.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.4
• /
• pp.438-445
• /
• 2015

Among several thermal wood modification methods German oil heating technology was applied to Korean pine specimens by heat treatment at $180^{\circ}C$ and $200^{\circ}C$. In addition the matched specimens were heat-treated by Thermowood method. The heat-treated specimens were planed and their colors were measured with a colorimeter at 1 mm and 4 mm below the surfaces. The average lightness index (L*) of Oil-180 specimens was the largest followed by Oil-200 and Tmo-200 specimens. The average redness indexes (a*) of all specimens were increased by heat treatment, while the average yellowness indexes (b*) were variable. The average color differences (${\Delta}E*$) of Oil-200 and Tmo-200 specimens were above 30.0, while that of Oil-180 specimens was only 18.4. It can be concluded that the colors of the heat-teated specimens were uniformly changed because their average color difference indexes (${\Delta}E*$) between the inner layers were below 6.0.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2002.05a
• /
• pp.49-52
• /
• 2002

경량 건축소재는 건축자재의 경량화, 고급화 및 다양화 등의 기능성 건축소재로서 역할을 요구하고 있으며 그 중 대표적인 것으로서는 polyurethane foamd, Cellulose, 무기 fiber 등이 건축소재로 이용되고 있다. Cellulose계의 wood material의 경우 건축폐재, 가로수의 전지나무 및 제재공장에서 발생하는 나무쓰레기, 대패밥 등과 폐신문지 등의 가공 후 폐기물이 발생하고 있으며 이러한 Cellulose계의 물질들은 고유한 습기의 조절능력, 단열특성을 가지고 있으나 Combustibility, rotting, warping 등의 단점을 가지고 있다 이러한 단점을 극복하기 위해 현대생활환경에 접근할 수 있는 새로운 cellulose계의 modification 및 기술적으로 많이 연구되어지고 있다.(중략)

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.1
• /
• pp.56-64
• /
• 2009

The purpose of this study was to investigate and develop an eco-friendly wood adhesive based on vegetable oil (especially soybean oil), the renewable and sustainable natural resources, using ozonification technology for the chemical structure modification. The soybean oil (SBO) was reacted with $O_3$ at the rate of 7.13 g/h for different times, 15 minutes, 30 minutes, 60 minutes, and 120 minutes. The investigation of the modified chemical structure of the ozonized SBOs were conducted using FT-IR, $^1H$-NMR, MALDI-TOF MS, and GC/MS. As ozonification time increased, the peak of the unsaturated double bonds was disappeared and aldehyde or carboxyl peak appeared because ozonification broke the oil into small molecules. The plywoods were made at $110^{\circ}C$ with 30 seconds/mm hot-press time using the different ozonized SBO/pMDI adhesives and were tested for the dry, wet, cyclic boil test according to the Korea Industrial Standard F3101 Ordinary plywood. The bond strengths gradually increased with increasing ozonification time. The weight ratio 1:1 (ozonized SBO/pMDI), all strengths in 15, 30 and 60 minuets, exceeded constantly the dry, wet, cyclic boiling standard requirement. The range of ozonification time and weight ratio can fulfil1 the requirment of the wet test standard were 30~60 minutes and more than 0.5 pMDI. From the comprehensive view on the results of above experiments, it could be confirmed through experiments that ozonized SBO/pMDI has characteristics of effective reactivity and wet stability showed as an excellent candidate of wood adhesive applications.

• Journal of Microbiology
• /
• v.45 no.6
• /
• pp.485-491
• /
• 2007

The effects of biological pretreatment on the Japanese red pine Pinus densiflora, was evaluated after exposure to three white rot fungi Ceriporia lacerata, Stereum hirsutum, and Polyporus brumalis. Change in chemical composition, structural modification, and their susceptibility to enzymatic saccharification in the degraded wood were analyzed. Of the three white rot fungi tested, S. hirsutum selectively degraded the lignin of this sortwood rather than the holocellulose component. After eight weeks of pretreatment with S. hirsutum, total weight loss was 10.7%, while lignin loss was the highest at 14.52% among the tested samples. However, holocellulose loss was lower at 7.81 % compared to those of C. lacerata and P. brumalis. Extracelluar enzymes from S. hirsutum showed higher activity of ligninase and lower activity of cellulase than those from other white rot fungi. Thus, total weight loss and changes in chemical composition of the Japanese red pine was well correlated with the enzyme activities related with lignin- and cellulose degradation in these fungi. Based on the data obtained from analysis of physical characterization of degraded wood by X-ray Diffractometry (XRD) and pore size distribution, S. hirsutum was considered as an effective potential fungus for biological pretreatment. In particular, the increase of available pore size of over 120 nm in pretreated wood powder with S. hirsutum made enzymes accessible for further enzymatic saccharification. When Japanese red pine chips treated with S. hirsutum were enzymatically saccharified using commercial enzymes (Cellulclast 1.5 L and Novozyme 188), sugar yield was greatly increased (21.01 %) compared to non-pre treated control samples, indicating that white rot fungus S. hirsutum provides an effective process in increasing sugar yield from woody biomass.