• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.1
• /
• pp.80-86
• /
• 2007

In this study we experimented setting time and basic properties as waste wood fiber and sodium silicate substitution rate to reuse waste wood fiber produced in construction field to wood chip board. To do this construction waste woods were crushed with the size less than 10mm, mixed with the rate of 1:2, 2.5, 3, and added sodium silicate with the rate of 0, 5% of cement content. The results are as follows. As the substitution rate of construction waste wood was increased delay of setting time was also increased, and the batch of adding 5% accelerator had a 13~17 hours faster setting time than non accelerator batch. The compressive strength was lower as wood substitution rate was higher, and as the specific gravity was higher, the strength was also higher. As wood substitution rate was higher, heat conductivity was lower, and as specific gravity was higher, heat conductivity also was higher.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.6
• /
• pp.490-496
• /
• 2013

The board using recycled wood waste chip tends to decrease in terms of physical and mechanical properties. The reasons are notably different shape of chips, components of used adhesive and impurity content, which bring the irregular quality and downgrading of board. More over, the board has higher emissivity of formaldehyde than regular board, because recycled chip contains adhesives that were used to make previous products. This low quality of products weakens the price and quality competitiveness, and it led to bringing the issue of problem in Korean board industry. For these reason, in this study, boards using byproducts of plywood were made to evaluate physical and mechanical properties according to manufacturing conditions. As a result, The board was consists of 4~16 mesh chips for core layer and veneer on both face and they were combined using EMDI, and its' bending strength was 57.7 $N/mm^2$ which is 215% higher than that of OSB (26.8 $N/mm^2$). Moreover, the emissivity of formaldehyde was 0.7 ppm, this board seems to substitute OSB for rated sheathing.

• Journal of the Korea Furniture Society
• /
• v.11 no.2
• /
• pp.67-72
• /
• 2000

Some physical characteristics as thickness swelling, heat conduction, and bending properties of composite hoards made of waste wood chip and charcoal were measured. Wood-charcoal composite boards of three types and cement board were prepared for this study as shown in Table 1, Keeping duration of strawberries in the boxes($25cm{\times}25cm{\times}25cm$) manufactured with the boards was also examined. Thickness swelling and bending properties(MOR and MOE) of board B and C were lower than those of board A. Among the wood-charcoal composite boards except cement board, there were no differences in heat conduction(mm/sec.). Strawberries in the box with board C were kept longer duration in fresh condition than that with cement board. From the results, it is suggested that wood-charcoal composite boards can be used for eco-material.

• Journal of the Korean Wood Science and Technology
• /
• v.15 no.3
• /
• pp.44-55
• /
• 1987

In order to study the effect of sawdustboard combined with plastic chips, 0.5mm($T_1$), 1mm($T_2$), 1.4mm($T_3$) thick nylon fiber. polypropylene rope fiber(RP), and 0.23mm thick moth-proof polypropylene net fiber(NP) were cut into 0.5, 1, 2cm long plastic chips. Thereafter, sawdustboard combined with plastic chips prepared as the above and plastic non-combined sawdustboard(control) were manufactured into 3 types of one-, two-, and three layer with 5 or 10% combination level. By the discussions and results at this study, the significant conclusions of mechanical and physical properties were summarized as follows: 1. The MORs were shown in the order of 3 layer> 2 layer> 1 layer among plastic non-combined boards, and $T_3$ < $T_2$ < $T_1$ < RP (NP(5%) < NP(l0%) among plastic combined boards. In 2cm long plastic chip in 1 layer board, the highest strength through all the composition was recognized. 1 layer board showing the lower strength with 0.5cm plastic chip rendered to the bending strength improvement by 2 or 3 layer board composition. On the other hand, 2 or 3 layer combined with 1, 2cm long polypropylene net fiber chips incurred MOR's conspicuous decrease requiring optimum plastic chip combined level and consideration to combined type. 2. MOE in plastic non-combined 3 layer board exhibited sandwich construction effect by higher resin content application to surface layer in the order of 3layer>1layer>2layer with the highest stiffness of the board combined with polypropylene chip, while nylon chip-combined board had little difference from plastic non-combined board. In relevant to length and layer effect, 3 layer board combined with the 0.5cm long polypropylene net fiber chip in 5% and 10% combined level presented 34-43% and 44-76% stiffness increase against plastic non-combined board(control), respectively. Moreover, in 1 layer board, 30% stiffness increase with 10% against 5% combined level in the 1 and 2cm long polypropylene net fiber chip was obtained. 3. Stress at proportional limit(Spl) showing the fiber relationship (r: 0.81-0.97) between MOR presented in the order of 1 layer<2 layer<3 layer in plastic non-combined board. Correspondingly, combined effect by layer and plastic chip length was similar to MOR's. 4. Differently from previous properties(MOR, MOE, Spl). work to maximum load(Wml) of 2 layer board approached to that of 3 layer board. Conforming the above phenomenon. 2 layer combined with 0.5cm long polypropylene net fiber chip kept the greater work than 1 layer. The polypropylene combined board superior to nylon -and plastic non - combined board seemed to have greater anti - failing capacity. 5. Internal bond strength(IB), in contrast to MOR's tendency. showed in the order of T1

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.4
• /
• pp.29-38
• /
• 1997

The effect and control of wood property of reconstituted composite panels for improved board properties by wood-waste materials and development of combination method for heterogeneous materials have been of interest to the wood science researchers. The purpose of this study is to consider the properties in relation to hot pressing conditions and to develope the optimum hot pressing condition with waste wood and waste tire for the manufacturing of composite boards. The study of composite boards for recycling of wood and waste tire is nothing up to the present. Physical and mechanical properties such as specific gravity, moisture content, swelling coefficient, modulus of rupture and modulus of elasticity in bending test were studied. The condition of 3-stage press time for the lowest moisture content of composite board was $4{\rightarrow}3{\rightarrow}3$ minutes. Specific gravity of composite panels was affected mainly by the amount of rubber chip. Because of the low rigidity and high elasticity in rubber chip, it is considered the composite panel was adequate material in the place of compression load, but not bending load. Therefore, it was concluded that a use of rubber-based wood composite panel is proper to the interior materials such as floor a room than exterior materials. From the test results, the most optimum hot pressing conditions were $4{\rightarrow}3{\rightarrow}3$ minutes for 3-stage press time and $45{\rightarrow}20{\rightarrow}5kg/cm^2$ for 3-stage press pressure. The rubber-based wood composite panel was very excellent in elasticity by combination of rubber chip in comparison with existing other wood-based materials. Therefore, it was considered that rubber-based wood composites can be applicable to every interior materials such as floor a room and will be expected to effective reuse and recycle of waste tires and wood-waste materials, and will be contribute to protection of environment pollution in earth.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.4
• /
• pp.57-64
• /
• 1999

This research was carried out to investigate the effects of density, resin and particle types on the physical and mechanical properties of the composites made from various wood particles mixed with coating paper. The experiment was designed to apply with three particles (flake, chip, and fiber) and three resin types (urea, phenol and PMDI resin). The mixed ratio of coating paper to wood particle was fixed on 50 to 50% in each board making. And also it was designed to apply for four density levels (0.6, 0.7, 0.8 and 0.9 g/$cm^3$) and four mixed formulations of coating paper to wood particle (10:90, 20:80, 30:70, and 40:60 %) to analyze clearly the effects of PMDI resin. Coating paper-wood particle composites have acceptable bending strength (MOR, MOE) though the mixed ratio of coating paper was increased, but have low internal bond strength and poor dimensional stability (WA, TS, LE). Composites with high density had higher mechanical properties but showed lower physical properties than composites with low density. In conclusion, at least up to 20% mixed ratios, coating paper-wood particle composites have acceptable physical and mechanical properties, and PMDI resin has possibility for coating paper-wood particle composite manufacture.

• Fire Science and Engineering
• /
• v.22 no.3
• /
• pp.208-215
• /
• 2008

Existent wood wool cement boards are low-quality cement boards made out of wood chip wastes. Recently, however, they are produced by making wood chips into fibrous forms to have good looks and excellent performances in sound absorption and thermal insulation. Though they have been broadly used in the advanced countries, they were rather expensive products with limited use in Korea having no domestic manufacturers of them. Since 2005, however, it has been possible for the boards to be used in various fields due to their lowered prices and stable supplies by the arrival of domestic manufacturers. For the purpose of encouraging broad use of the boards, this research aims to explore their practical applications by way of assessing the flame retardant and fire resistant performances when they are applied to dry-wall system.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.1
• /
• pp.79-87
• /
• 2008

Many researchers have studied on rooftop greening that can be installed in abandoned spaces on a building roof. The most important issue in rooftop greening is the soil weight problem. The light greening materials are needed to solve this problem. Therefore, many alternative materials against the soil were investigated for rooftop greening. In this study, the waste wood chips and the waste paper slurry were evaluated as the lightweight vegetation foundation for rooftop greening. It also has a meaning for recycling of waste materials. The mixture ratio of waste wood chips to waste paper slurry for the board (the foundation of greening) was 60 to 40. The wet strength resin and the sizing agent were additionally added with different amount. After the forming of the board, physical and chemical properties were tested with the variation of wet strength resin and sizing agent. As the result of the test, the board with 15% of wet strength resin in the wet condition showed the highest strength. Futhermore, the moisture evaporation loss from the board surface with sizing agent was much lower than that from the board without sizing agent. Therefore, it was clear that the sizing agent was effective for water retention. The change of thickness in the wet condition was less than 1 mm, and it showed that the board is the predominant material on the dimensional stability. The average pH value of the board was ranged from 7.6 to 8.25.

• Journal of Forest and Environmental Science
• /
• v.18 no.1
• /
• pp.61-72
• /
• 2001

The study was carried out to investigate the surroundings and benefit analysis on the planting investment of Thailand for securing a stable supply of timber through overseas planting, The results show that Thailand government is planing to increase the coverage of forest from 25% to 40%, encouraging planting over the country. More advantages and incentives are given in the investments in planting and wood-processing industries such as plywood, veneer, and chip & hard board, etc. In Thailand Eucalyptus species which are most popular in planting as they are lucratively used as a material of pulp. The Internal rate of return (IRR) in the study was ranged from 29.1 % to 59.3.

• Journal of the Korean Wood Science and Technology
• /
• v.16 no.2
• /
• pp.1-41
• /
• 1988

For the purpose of utilizing the sawdust having poor combining properties as board raw material and resulting in dimensional instability of board, polypropylene chip (abbreviated below as PP chip) or oriented PP thread was combined with sawdust particle from white meranti(Shorea sp.). The PP chip was prepared from PP thread in length of 0.25, 0.5, 1.0 and 1.5 cm for conventional blending application. Thereafter, the PP chip cut as above was combined with the sawdust particle by 3, 6, 9, 12 and 15% on the weight basis of board. Oriented PP threads were aligned with spacing of 0.5, 1.0 and 1.5cm along transverse direction of board. The physical and mechanical properties on one, two and three layer boards manufactured with the above combining conditions were investigated. The conclusions obtained at this study were summarized as follows: 1. In thickness swelling, all one layer boards combined with PP chips showed lower values than control sawdustboard, and gradually clear decreasing tendendy with the increase of PP chip composition. Two layer board showed higher swelling value than one layer board, but the majority of boards lower values than control sawdustboard. All three layer boards showed lower swelling values than control sawdustboard. 2. In the PP chip and oriented thread combining board, the swelling values of boards combining 0.5cm spacing oriented thread with 1.0 or 1.5cm long PP chip in 12 and 15% by board weight were much lower than the lowest of one or three layer. 3. In specific gravity of 0.51, modulus of rupture of one layer board combined with 3% PP chip showed higher value than control sawdustboard. However, moduli of rupture of the boards with every PP chip composition did not exceed 80kgf/cm2, the low limit value of type 100 board, Korean Industrial Standard KS F 3104 Particleboards. Moduli of rupture of 6%, 1.5cm-long and 3% PP chip combined boards in specific gravity of 0.63 as well as PP chip combined board in specific gravity of 0.72 exceeded 80kgf/$cm^2$ on KS F 3104. Two layer boards combined with every PI' chip composition showed lower values than control sawdustboard and one layer board. Three layer boards combined with.1.5cm long PP chip in 3, 6 and 9% combination level showed higher values than control sawdustboard, and exceeded 80kgf/$cm^2$ on KS F 3104. 4. In modulus of rupture of PP thread oriented sawdustboard, 0.5cm spacing oriented board showed the highest value, and 1.0 and 1.5cm spacing oriented boards lower values than the 0.5cm. However, all PP thread oriented sawdustboards showed higher values than control saw-dustboard. 5. Moduli of rupture in the majority of PP chip and oriented thread combining boards were higher than 80kgf/$cm^2$ on KS F 3104. Moduli of rupture in the boards combining longer PP chip with narrower 0.5cm spacing oriented thread showed high values. In accordance with the spacing increase of oriented thread, moduli of rupture in the PP chip and oriented thread combining boards showed increasing tendency compared with oriented sawdustboard. 6. Moduli of elasticity in one, two and three layer boards were lower than those of control sawdustboard, however, moduli of elasticity of oriented sawdustboards with 0.5, 1.0 and 1.5cm spacing increased 20, 18 and 10% compared with control sawdustboard, respectively. 7. Moduli of elasticity in the majority of PP chip and oriented thread combining boards in 0.5, 1.0 and 1.5cm oriented spacing showed much higher values than control sawdustboard. On the whole, moduli of elasticity in the oriented boards combined with 9% or less combination level and 0.5cm or more length of PP chip showed higher values than oriented sawdustboard. The increasing effect on modulus of elasticity was shown by the PP chip composition in oriented board with narrow spacing. 8. Internal bond strengths of all one layer PP chip combined boards showed lower values than control sawdust board, however, the PP chip combined boards in specific gravity of 0.63 and 0.72 exceeded 1.5kgf/$cm^2$, the low limit value of type 100 board and 3kgf/$cm^2$, type 200 board on KS F 3104, respectively. And also most of all two, three layer-and oriented boards exceeded 3kgf/$cm^2$ on KS F. 9. In general, screw holding strength of one layer board combined with PP chip showed lower value than control sawdustboard, however, that of two or three layer board combined with PP chip did no decreased tendency, and even screw holding strength with the increase of PP chip composition. In the PP chip and oriented PP thread combining boards, most of the boards showed higher values than control sawdustboard in 9% or less PP chip composition.