• 한국표면공학회지
• /
• 제30권2호
• /
• pp.144-154
• /
• 1997

Effects of plasma nitriding on the surface charcteristice of stainless steel(SS) were investjgated by utilizing wear tester, micro-hardness tester and potentiostat. The surface and corrosion morphology of plasma nitrided SS were analyzed by utilizing optical microscopy, SEM, XRD and WDX. It was found that plasma nitriding at $550^{\circ}C$, compared with $380^{\circ}C$, prodiced a good wear resistance and hardness as nitriding time increased, whereas Mo addition showd that were resistance and hardness decreased. Intergranular corrosion(IGC) resistance improved significantly in the case of plasma nirtrided SS containing 4.05wt% Mo at $380^{\circ}C$ because that nitrogen and Mo ast syner gidically to form a protective layer on surface which is responsible for the aggresive SCN-ion. Plasma nitrided at $550^{\circ}C$ decreased IGC as Mo content increased. Pitting improved in the plasma nitirided SS at Mo content incresased owing to retard a nucleation and growth of chromium carbide or nitirde in grain boundary.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.111-112
• /
• 2006

Injection molding of corrosive super engineering plastics and engineering plastics with various fillers is conducted under severe conditions and causes corrosion and wear problems. We have developed $Mo_2NiB_2$ boride base cermets, which have excellent corrosion-and wear-resistances, and tried to apply them into plastic molding machine parts. In this paper, the effects of V substitution for Cr on the mechanical properties, corrosion resistance and microstructure of Ni-5.0B-51.0Mo-(17.5-X)Cr-XV (mass%) model cermets were investigated. Both transverse rupture strength (TRS) and hardness increased monotonically with increasing V content and reached 2.94GPa and $87.2R_A$ at 10.0%V, respectively. The improvements of TRS and hardness were attributed to microstructural refinement.

• Corrosion Science and Technology
• /
• 제5권2호
• /
• pp.52-61
• /
• 2006

Recently, much of the current development in surface modification engineering are focused on multilayered coatings. Multilayered coatings have the potential to improve the tribological properties. Four different multilayered coatings were deposited on AISI D2 steel. The prepared samples are designed as $WC-Ti_{0.6}Al_{0.4}N$, $WC-Ti_{0.53}Al_{0.47}N$, $WC-Ti_{0.5}Al_{0.5}N$ and $WC-Ti_{0.43}Al_{0.57}N$. The multilayered coatings were investigated with respect to coating surface and cross-sectional morphology, roughness, adhesion, hardness, porosity and tribological behavior. Especially, wear tests of four multilayered coatings were performed by using a ball-on-disc configuration with a linear sliding speed of 0.017 m/sec, 5.38 N load. The tests were carried out at room temperature in air by employing AISI 52100 steel ball ($H_R=66$) having a diameter of 10 mm. The surface morphology, and topography of the wear scars of samples and balls have been determined by using scanning electron spectroscopy (SEM). Results have showed an improved wear resistance of the $WC-Ti_{1-x}Al_xN$ coatings with increasing of Al concentration. $WC-Ti_{0.43}Al_{0.57}N$ coating with the lower surface roughness and porosity with good adhesion enhanced wear resistance.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2002년도 춘계학술발표회 초록집
• /
• pp.36-36
• /
• 2002

Effects of pulse-plating on the wear and corrosion resistance of chrome-carbon layers were studied. The plating were carried out at $06A/\textrm{cm}^2$ in modified Sargent bath containing formic acid at $53^{\circ}C$. The chrome layer were super-saturated with carbon up to 2.0wt. %, which precipitated as chrome carbide such as $Cr_{23}C_6$ after vacuum aging above $200^{\circ}C$ for 1 hour. This resulted in improvement of hardness and wear resistance of the chrome layer. Considering the reduction of corrosion resistance due to the thermal effect, optimum vacuum aging condition of the chrome layer in this study was I-hour at $200^{\circ}C$.

• Journal of Welding and Joining
• /
• 제21권2호
• /
• pp.42-49
• /
• 2003

The protection of steel surfaces against wear is a practical problem far agricultural, mining and manufacturing industries. Commercial processes are available in which a hard tungsten carbides rich steel layer is formed on the surface of carbon steel digging, drilling and gouging tools to improve their wear resistance. The nature of the interaction of the tungsten carbide with the steel matrix is important in determining the wear and corrosion properties of the resulting metal matrix composites(MMC). In the study, WC-12%Co/low carbon steel MMC overlays have been prepared by gas metal arc welding(GMAW) according to size of WC-12%Co grits. The characteristics wear resistance and wear mechanism have been investigated in relation to the experiment conditions each other. After MMC overlay had been tested by rubber wheel abrasion test, it was known that MMC overlay has a excellent wear resistance. Fe$_{6}$W$_{6}$C carbides of matrix in overlays were not important to restrain rubber wheal abrasion wear. Wear loss is proportioned to a applied load according to time. On the case of low load, wear occurred severely in the matrix of overlay more than WC-12%Co grit, on the contrary it is reverse on the case of high load because of fracture of WC-12%Co grits.its.

• International Journal of Automotive Technology
• /
• 제7권1호
• /
• pp.75-82
• /
• 2006

Fretting corrosion widely known as a degradation mechanism refers to the combination of fretting wear and corrosion such as oxidation. This paper critically reviews the works published previously on fretting corrosion of electrical connectors. Various experimental approaches such as testing machines, material selection, testing environments, acceleration testing techniques and preventing methods are addressed. Future research prospects are suggested.

• 대한금속재료학회지
• /
• 제50권11호
• /
• pp.801-808
• /
• 2012

TiAlCN coatings with various C contents were synthesized by unbalanced magnetron sputtering. The characteristics, the crystalline structure, surface morphology, hardness, and friction coefficient of the coatings as a function of the C content were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), a microhardness tester, and a wear test. In addition, their corrosion behaviors in a deaerated 3.5 wt% NaCl solution at $40^{\circ}C$ were investigated by potentiodynamic polarization tests. The results indicated that the $Ti_{14.9}Al_{15.5}C_{30.7}N_{38.9}$ coating had the highest hardness, elastic modulus, and a plastic deformation resistance of 39 GPa, 359 GPa, and 0.55, respectively, and it also had the lowest friction coefficient of approximately 0.26. Comparative evaluation of the TiAlCN coatings indicated that a wide range of coating properties, especially coating hardness, could be obtained by the synthesis methods and processing variables. The microhardness of the coatings was much higher than that from previously reported coating using similar magnetron sputtering processes. It was almost as high as the microhardness measured from the TiAlCN coatings (~41 GPa) synthesized using an arc ion plating process. The potentiodynamic test showed that the corrosion resistance of the TiAlCN coatings was significantly better than the TiAlN coatings, and their corrosion current density ($i_{corr}$), corrosion potentials ($E_{corr}$) and corrosion rate decreased with an increasing C content in the coatings. The much denser microstructure of the coatings due to the increased amount of amorphous phase with increasing C contents in the coatings could result in the the improved corrosion resistance of the coatings.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1995년도 춘계학술대회 논문집
• /
• pp.3-20
• /
• 1995

Advanced ceramics have excellent thermal resistance, wear resistance, corrosion resistance, and other properties, and are promising materials as structural materials. Over the past decade, they have been applied to some machine parts, for example, glow plugs and turbochargers of automotive engines. In the case where the advanced ceramics are used as these structural parts, te low-dimensional accuracy of sintered bodies requires secondary machining.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.7-11
• /
• 2013

High velocity oxy-fuel (HVOF) spray coating of WC-metal powder (powder) was carried out to improve the resistances of friction, wear and corrosion of magnetic bearing shaft material Inconel718 (In718) of turbo blower. A micron sized WC-metal powder (86.5% WC, 9.5% Co 4% Cr) was coated onto In718 surface using HVOF thermal spraying. During the spraying, the binder metals and alloy such as Co, Cr and Co-Cr alloy were molten and a small portion of WC particles were partially decomposed to $W_2C$ and free carbon at above its decomposition temperature of $1250^{\circ}C$. The free carbon and excessively sprayed oxygen formed carbon oxide gases, resulting a porous coating of porosity of $2.2{\pm}0.3%$. The surface hardness of substrate increased approximately three times from 400 Hv of In718 to $1260{\pm}30Hv$ of the coating The friction coefficients of the coating were approximately $0.33{\pm}0.03$ at $25^{\circ}C$ and $0.26{\pm}0.03$ at $450^{\circ}C$. These values were smaller than those of In718 substrate at both temperatures due to the lubrication from the free carbon and the cobalt oxide debris. The corrosion resistance of the coating was higher than that of In718 both in salt water of 3.5% NaCl and acid of 1 M HCl solutions, on the contrary, it was lower in base solution of 1 M NaOH. According to this study, the HVOF WC-metal powder coating is recommended for the durability improvement of magnetic bearing shaft of turbo blower.

• Tribology and Lubricants
• /
• 제40권3호
• /
• pp.97-102
• /
• 2024

The next-generation Molten Salt Reactor is known for its high safety because it uses nuclear fuel dissolved in high-temperature molten salt, unlike traditional solid atomic fuel methods. However, the high-temperature molten salt causes severe corrosion in internal structural materials, threatening the reactor's safety. Therefore, it is crucial to investigate the high-temperature corrosion resistance and wear performance of materials used in reactors to ensure safety. In this study, the high-temperature corrosion resistances and wear performances of corrosion samples in a NaCl-MgCl2-KCl (20-40-40 [wt%]) molten salt are investigated to evaluate the applicability of economically viable stainless steels, 316SS and 304SS. Hastelloy C276 and a new alloy containing a small amount of Nb are used as reference samples for comparative analysis. The mass loss, mass loss rate per unit volume, and surface roughness of each sample are measured to understand the corrosion mechanisms. Scanning electron microscopy and energy-dispersive spectroscopy analyses are employed to analyze the corrosion mechanisms. Wear tests on the corroded samples are also conducted to assess the extent of corrosion. Based on the experimental results, we predict the lifespans of the materials and evaluate their suitability as candidate materials for molten salt reactors. The data obtained from the experiments provide a valuable database for structural materials that can enhance the stability of molten salt reactors and recommend high-temperature corrosion-resistant materials suitable for next-generation reactors.