• Journal of Adhesion and Interface
• /
• v.7 no.1
• /
• pp.3-9
• /
• 2006

Three isocyanate groups of IP-$75^{(R)}$ and one hydroxyl group of various amino alcohols were applied for preparing cationic type water-borne polyurthane (PU) having ionic center onto flexible side chains. Average particle size, dispersion stability, viscosity, contact angle, surface energy, glass transition temperature ($T_g$), and adhesion strength of prepared water-borne PUs were measured and analyzed with different NCO/OH mol ratios, ionomers, and neutralizing agents. It was characterized that the prepared PU has a smaller particle size and a better dispersion stability than the conventional cationic water-borne PU containing ionic centers onto main chains.

• Applied Chemistry for Engineering
• /
• v.27 no.2
• /
• pp.221-226
• /
• 2016

Production of eco-friendly and biologically harmless materials is strongly required in all industries. In particular, reducing volatile organic compounds in coating processes is extremely important to secure worker's safety. During recent two decades, extensive research works on water-borne polyurethane dispersion (PUD) have been continuously developed as an alternative to solvent-borne polyurethane. However, PUD was shown inferior mechanical properties to the organic solvent-borne polyurethane due to a limit to the molecular weight increase, which resulted in the limit of applications. To overcome this drawback, several approaches have been examined such as polymer blends and thermal/radiation induced crosslinking. Among these methods, the radiation curing system was suitable for industrialization because of the high crosslinking density and fast curing speed. In this study, we overcame the drawback for PUD via introducing benzophenone radiation curable units to PUD. We synthesized PUD films which possessed good dispersion in water for 30 days, increased Tg and Td more than $5^{\circ}C$ after UV curing film as well as improved young's modulus more than double.

• Journal of the Korean Applied Science and Technology
• /
• v.39 no.6
• /
• pp.924-931
• /
• 2022

Undenatured castor oil and trimethylolpropane (TMP) were used to obtain bio-based water-based polyurethane. Isophorone diisocyanate (IPDI) was incorporated into the formulation to obtain a transparent film, and ethylenediamine (EDA) was used for chain extension. In order to measure the change in physical properties according to the contents of castor oil and TMP, each tensile strength, elongation, and abrasion resistance test was conducted. As the contents of castor oil and TMP increased, the tensile strength increased, the elongation decreased, and the surface hardened strongly as the respective contents increased.