• Journal of the Korean Wood Science and Technology
• /
• v.38 no.6
• /
• pp.587-601
• /
• 2010

This review attempted to overview characteristics of nanocellulose from various sources, its isolation methods, and properties of nanocellulose-based nanocomposites. Currently, nanocelluloses could be obtained from a variety of cellulose sources, including wood pulp, tunicate, bacterial cellulose etc., and are isolated by various ways such as chemical, physical, or biological methods. The length and width of nanocellulose is in the range of 100~300 nm long and 5~50 nm wide although characteristics of nanocellulose shows a wide variability, depending on sources and isolation method. Nanocellulose is also being used as a reinforcement in the nanocomposites via various methods. Many water soluble polymers were reinforced by the incorporation of nanocellulose, which significantly improves tensile and storage moduli of the nanocomposites. In order to be used for hydrophobic polymers, the surface of nanocellulose was modified. Even though there is a significant progress in the utilization of nanocellulose as a reinforcement of polymers, further research is required to find a niche market of nanocellulose-reinforced nanocomposites. In addition, isolation methods of producing the nanocellulose in a large quantity for commercial applications should be developed to extend the application of nanocellulose-based bio-nanocomposites in future.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.4
• /
• pp.24-30
• /
• 2003

In order to develop structural 'bamboo zephyr board', properties of boards produced by various methods making zephyr were estimated. All of boards were tested with KS(Korean Standards) F 3014 Particle board, and results were summarized as follow. The zephyr boards produced by final 1.5 mm roller space had the best properties(MOR, MOE and IB strength) among boards produced by different final roller space. Also, they had the best properties(MOR and MOE) in bending test after 1 hour soaking treatment after 2 hour-boiling in water, which were similar to properties of boards in dry-condition. Thickness swelling(TS) of all boards was less than 12% required to the Korean Standards A 3014. Zephyr boards produced by final 1.5 mm roller space also had the lowest values among all of boards. Boards produced by non-treatment (in green condition) had the better strength than those of boards produced by different pre-treatment methods(boiling in water and in 0.3% NaOH) in bending test.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.48 no.3
• /
• pp.57-65
• /
• 2016

Indigo (Polygonum tinctorium L.) is a typical blue dye which had been used from ancient times. This study was going to shade the complicated traditional methods extracting indigo dye by the fermentation and producing as adsorbate on calcium hydroxide, which says so called as the 'Indigo lime'. Accordingly we were going to make indigo through the hydrolysis of the hot water extractives of indigo leaves simply. During hot-water extraction, ${\beta}$-glucosidase which required hydrolysis of the linkage between indigo and glucose was not activated. To achieve this goal, indican was acid-hydrolyzed to glucose and indigo. The acetic acid, citric acid, hydrochloric acid, and sulfuric acid were used for the hydrolysis of hot water extractives. The hydrolysis conditions of extractives performed in water bath at $80^{\circ}C$ for 120 minutes and in an autoclave for 120 minutes. In the acid hydrolysis of extracted indican by hot water, the indican yields of acetic acid and hydrochloric acid hydrolysis were higher than sulfuric acid in water bath. Also, the indican yield of hydrochloric acid hydrolysis was better than sulfuric acid in autoclave. The hot water extracted indican was confirmed by HPLC analysis and its structure was confirmed by UV-Vis and FT-IR spectroscopy, compared with isolated indigo and commercial synthesized indigo. This improved extraction and hydrolysis methods can be replace the traditional indigo making method.

• Journal of the Korean Applied Science and Technology
• /
• v.34 no.1
• /
• pp.1-11
• /
• 2017

Bio-oil has attracted considerable interest as one of the promising renewable energy resources because it can be used as a feedstock in conventional petroleum refineries for the production of high value chemicals or next-generation hydrocarbon fuels. Zeolites have been shown to effectively promote cracking reactions during pyrolysis resulting in highly deoxygenated and hydrocarbon-rich compounds and stable pyrolysis oil products. In this study, catalytic pyrolysis was applied to upgrade bio-oil from yellow poplar and then fuel characteristics of upgraded bio-oil was investigated. Yellow Poplar(500 g) which ground 0.3~1.4 mm was processed into bio-oil by catalytic pyrolysis for 1.64 seconds at $465^{\circ}C$ with Control, Blaccoal, Whitecoal, ZeoliteY and ZSM-5. Under the catalyst conditions, bio-oil productions decreased from 54.0%(Control) to 51.4 ~ 53.5%, except 56.2%(Blackcoal). HHV(High heating value) of upgraded bio-oil was more lower than crude bio-oil while the water content increased from 37.4% to 37.4 ~ 45.2%. But the other properties were improved significantly. Under the upgrading conditions, ash and TAN(Total Acid Number) is decrease and particularly important as transportation fuel, the viscosity of bio-oil decreased from 6,933 cP(Control) to 2,578 ~ 4,627 cP. In addition, ZeoliteY was most effective on producing aromatic hydrocarbons and decreasing of from the catalytic pyrolysis.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.3
• /
• pp.1-8
• /
• 2000

To develop the technology of producing structural board from low grade materials, an attempt was made to produce strand/particle composites from split wood strand(S) and particle(P) of (Cryptomeria japonica D. Don), which changed the layer construction and the ratio of S/P. The influence of layer construction on board properties was determined, focusing on the number and alignment of the S layers. The effect of weight ratio of S/P (3:7, 1:1, 7:3) on mechanical properties was also discussed on seven layered panel. Mechanical properties were determined from static bending tests to give parallel and perpendicular modulus of rupture (MOR) and modulus of elasticity (MOE), and the internal bond (IB) strength. In general, the surface strand layers contributed to the MOR and MOE. The parallel MOR and MOE values were the largest for the single layered S panel (only Slayers: S1), but the perpendicular MOR and MOE was the smallest. Perpendicular MOR and MOE were the largest for seven layered composite that had two cross oriented strand layers (SPSPSPS: SP7). Specimens retained more than half of their MOE and MOR after two hours in boiling water and one hour soaking. IB was the largest for the panel having only P layers, however, differences in IB strength were not identified among the other multi-layered composite panels thus the effect of layer construction on IB strength was small. Thickness swelling (TS) and surface roughness were smaller for the composite having P layers on the surface than for those having S layers. The addition of strands did not enhance the mechanical properties (MOR, MOE, IB). TS values for the panels, with which the S/P ratio was over than 1:1, was the similar to the value for the single layered S panels.

• Journal of the Korean Wood Science and Technology
• /
• v.17 no.1
• /
• pp.3-11
• /
• 1989

This study was carried out to investigate the physical and mechanical properties. durability of adhesive bond and paint film for the basic data which were required to determine the suitability as a raw material for furniture the laminated veneer lumber (LVL) with pitch pine (Pinus rigida Mill). The results obtained were as follows; 1) The proper pressing time for making the LVL was over 45 second per milimeter of LVL thickness. 2) The bending strength of the LVL was lower than that of the solid wood but the compressive strength of the LVL was similar to that of the solid wood. The strength increased with the decrease of veneer thickness. 3) The impact bending absorbed energy of the LVL was 0 to 0.3 kg.m/$cm^2$ in the direction of parallel to the grain. The energy of the LVL was lower than that of the solid wood (0.68 kg.m/$cm^2$). 4) In warm water soaking and cold-dry tests, delamination of adhered layers surface crack, swelling, and color change were not found when the hot pressing time was over 45 second per milimeter of LVL thickness. As a result of soak under vacuum test shrinkage in the direction of parallel to the grain was about -1.0 percent and. was about 3.0 percent in the direction of the perpendicular to the grain. 6) The film cacks on the LVL's surface after the wet and cold-dry test were not found at all. 7) In the use of the LVL for interior decoration it was considered that the surface of the LVL be overlaid crossly with fancy veneers of birch and paulownia, etc. This cross overlayirg methods have resulted in few cracks on the fancy veneer.

• Fire Science and Engineering
• /
• v.29 no.2
• /
• pp.79-83
• /
• 2015

The fire accident is a representative type of disaster that can largely impact on business. Therefore, precautionary measures and rapid initial response is very important when a disaster occurs. The storage of porous combustibles is inevitable in coal yard, plywood processing industry, and others that are currently operating. Initial fire fighting of fire and identifying the ignition point in such a porous combustible storage space are so difficult that if the initial response is failed, being led to deep-seated fire, surface fire is likely to result in secondary damage. In addition, deep-seated fire can cause personal injuries and property damage due to a large amount of toxic gases and reignition. Therefore damage reduction measures is required around the storage space to handle a porous flammable. Improving the penetration performance of the concentration of the surfactant is carried out as underlying study, which is about an deep-seated fire extinguishing efficiency augmentation when using wetting agents. The porous materials used in the experiments is radiata pine wood flour, which occupies more than 75% of the domestic wood market. Fire fighting water is selected as Butyl Di Glycol (BDG), which is being used for infiltration extinguishing agent, and the experiment was carried out by producing a standard solution. The experiment was carried out on the basis of the Deep-Seated Fire Test of NFPA 18. The amount of watering, porous material to the internal amount of penetration, and runoff measurement out of the porous material was conducted. According to experimental results, as the surface tension is reduced, the surfactant concentration macroscopic penetration rate decreases, but infiltration to a porous material is shown to have growth characteristics.

• Journal of Conservation Science
• /
• v.32 no.2
• /
• pp.249-259
• /
• 2016

Effect of the flame retardants on Dancheong is studied in the present work. Two kinds of flame retardants were applied on Dancheong specimens and compared with control groups on which distilled water was applied instead of the flame retardants. The flame retardants enhanced the hygroscopic property of the surface of Dancheong. Furthermore, the added flame retardants reacted with oyster shell white($CaCO_3$) and lead red($Pb_3O_4$), producing new chemical compounds like Calcium phosphate tribasic and Lead Phosphates which make the painted layer of Dancheong dissolving and whitening over certain period of time. When applied in excessive amount and exposed in repetitive wet and dry condition, especially, they aggravate the surface problems significantly. These results will provide a good reference on the study of the discoloring/whitening effect of Dancheong layers at many traditional wooden building in Korea.

• Biotechnology and Bioprocess Engineering:BBE
• /
• v.10 no.6
• /
• pp.482-493
• /
• 2005

Biomass is originally photosynthesized from inorgainic compounds such as $CO_2$, minerals, water and solar energy. Recent studies have shown that anaerobic bacteria have the ability to convert recalcitrant biomass such as cellullosic or chitinoic materials to useful compounds. The biomass containing agricultural waste, unutilized wood and other garbage is expected to utilize as feed, food and fuel by microbial degradation and other metabolic functions. In this study we isolated several anaerobic, cellulolytic and chitinolytic bacteria from rumen fluid, compost and soil to study their related enzymes and genes. The anaerobic and cellulolytic bacteria, Clostridium thermocellum, Clostridium stercorarium, and Clostridium josui, were isolated from compost and the chitinolytic Clostridium paraputrificum from beach soil and Ruminococcus albus was isolated from cow rumen. After isolation, novel cellulase and xylanase genes from these anaerobes were cloned and expressed in Escherichia coli. The properties of the cloned enzymes showed that some of them were the components of the enzyme (cellulase) complex, i.e., cellulosome, which is known to form complexes by binding cohesin domains on the cellulase integrating protein (Cip: or core protein) and dockerin domains on the enzymes. Several dockerin and cohesin polypeptides were independently produced by E. coli and their binding properties were specified with BIAcore by measuring surface plasmon resonance. Three pairs of cohesin-dockerin with differing binding specificities were selected. Two of their genes encoding their respective cohesin polypeptides were combined to one gene and expressed in E. coli as a chimeric core protein, on which two dockerin-dehydrogenase chimeras, the dockerin-formaldehyde dehydrogenase and the dockerin-NADH dehydrogenase are planning to bind for catalyzing $CO_2$ reduction to formic acid by feeding NADH. This reaction may represent a novel strategy for the reduction of the green house gases. Enzymes from the anaerobes were also expressed in tobacco and rice plants. The activity of a xylanase from C. stercorarium was detected in leaves, stems, and rice grain under the control of CaMV35S promoter. The digestibility of transgenic rice leaves in goat rumen was slightly accelerated. C. paraputrificum was found to solubilize shrimp shells and chitin to generate hydrogen gas. Hydrogen productivity (1.7 mol $H_2/mol$ glucos) of the organism was improved up to 1.8 times by additional expression of the own hydrogenase gene in C. paraputrficum using a modified vector of Clostridiu, perfringens. The hydrygen producing microflora from soil, garbage and dried pelletted garbage, known as refuse derived fuel(RDF), were also found to be effective in converting biomass waste to hydrogen gas.