To prepare the waterborne silicone acrylic resin coatings, acrylic resin was prepared by a radical polymerization. Glass transition temperature(Tg) of the acrylic copolymer was fixed at 30℃ and the contents of tertiary amine monomer(DMAEMA), were varied to be 5, 10, 15 and 20 wt%, hydroxyl monomer, and carboxyl monomer were fixed 10 wt%, and 4 wt% respectively. γ-Glycidoxypropyltrimethoxysilane(GPTMS) containing epoxy group was used for curing agents. The eqivalent ratio of amine to epoxy was 1:1. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The gloss retension and color difference were improved at low tertiary amine concentration. The coatings containing 10wt% tertiary amine concentration have especially good weather resistant properties.

• Journal of Adhesion and Interface
• /
• v.8 no.1
• /
• pp.8-14
• /
• 2007

Poly(urethane-methyl methacrylate) hybrid emulsions can be controlled with their thermal, mechanical and anti-chemical properties as plastic coating materials. In this study, water dispersed poly(urethane-methyl methacrylate) hybrid emulsions were prepared by prepolymer synthesis and soap free emulsion polymerization. For imparting hydrophilicity on polyurethane prepolymer, 2,2-bis (hydroxymethyl) propionic acid was added to the polyurethane prepolymer with methyl methacrylate monomer and was neutralizated by triethylamine (TEA). After neutralization, the prepolymer mixture was dispersed in the water phase with stable droplets. The synthesis was carried out with chain extension from the ethylene diamine and initiation of methyl methacrylate by soap free emulsion polymerization. Stable poly(urethane-methyl methacrylate) hybrid emulsion was successfully obtained with different synthetic conditions and acrylic monomer contents. Poly(urethane-methyl methacrylate) hybrid emulsion were characterized and compared with tensile strength, viscosity, and adhesion properties.