• Polymer(Korea)
• /
• v.35 no.4
• /
• pp.342-349
• /
• 2011

The effect of the amount of vinyltriethoxysilane (VTEOS) in precipitated silica filled silicone rubbers was extensively investigated in terms of the change of mechanical properties, heat resistance, oil resistance, compression set, resilience, and curing characteristics. As the content of VTEOS increased from 0 to 2.0 phr, the hardness of the silicone rubber increased, however, tensile strength, elongation at break, and tear strength decreased. From heat resistance test, the change of mechanical properties was pronounced for silicone rubber treated with more VTOES. The best heat resistance was achieved at 2.0 phr VTOES. In addition, oil resistance was proportionally improved with VTEOS content. From oil resistance test. it was found that the decrease in hardness and maximum elongation was reduced for VTEOS-added systems. Finally, resilience, compression set, degree of cure and crosslink density were significantly enhanced with the amount of VTEOS.

• Korean Chemical Engineering Research
• /
• v.46 no.2
• /
• pp.310-315
• /
• 2008

Organic-inorganic hybrid solutions were made using glycidoxypropyl trimethoxysilane (GPTMS) and vinyltriethoxysilane (VTES) as starting materials by sol-gel method. Photochromic coating solutions were prepared by mixing the solution of photochromic dye (spiropyran) dissolved in ethylacetate with the organic-inorganic hybrid solutions. Photochromic films were prepared on polycarbonate sheets by spin coating and cured for 2 h at $100^{\circ}C$. The resulting films exhibited a reversible color change upon irradiation with UV light from transparent to blue. The color-fading speed and pencil hardness of the coating films increased with increasing the GPTMS content in the coating solutions.

• Journal of the Korean Magnetic Resonance Society
• /
• v.4 no.2
• /
• pp.91-102
• /
• 2000

The photoproduced cation radical of N-methylphenothiazine doped in the different kind of matrices of phenyltriethoxysilane (PhiTEOS), vinyltriethoxysilane (VTEOS), and methyloiethoxysilane (METOS) was comparatively studied with electron spin resonance (ESR) and electron nuclear double resonance (ENDOR). The photoinduced charge separation efficiency was determined by integration of ESR spectra which correspond to the amount of photoproduced cation radical in the matrices. This was correlatively studied with the polarity and pore size of the gel matrices. The polarity of the matrices was comparatively determined by measuring λ$\sub$max/ values of PC$_1$ in the different matrices. The relative pore size among the matrices was determined by measuring relative proton matrix ENDOR line widths of the photoproduced cation radical of PCI. The decay kinetic constants of the cation radical of PCI in the different matrices was relatively studied with fitting the biexponential decay curves after exposure into the ambient condition. This is correlatively interpreted with the polarity and pore size of the matrices.

• Clean Technology
• /
• v.18 no.1
• /
• pp.57-62
• /
• 2012

Aqueous poly (vinyl alcohol) (PVA) solution was modified by using hydrophobic vinyltriethoxysilane (VTEOS) and then adding different amounts of poly (acrylic acid) (PAA) to the resulting solution. Thermal and mechanical properties, contact angle, water vapor transmission rate (MVTR) and oxygen gas transmission rate ($O_2TR$) of the film samples fabricated by these solutions were investigated. The glass transition temperature (Tg) of the VTEOS-modified films was sightly increased and the value remained unchanged according to the amount of PAA. The tensile strength of the VTEOS-modified films was found to be 9.48~10.72 $kg/mm^2$ which showed no significant difference compared with that of PVA. The film prepared with VTEOS-modified PVA/PAA (= 90/10), of which the swelling and solubility were measured to be 198% and 0%, respectively, showed improved water-resistance. The MVTR and $O_2TR$ for the PET film (thickness 50 ${\mu}m$) coated with VTEOS-modified PVA/PAA (= 90/10) film (thickness 2.5 ${\mu}m$) were measured to be 11.04 $g/m^2/day$ and 3.1 $cc/m^2/day$, respectively.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.430-435
• /
• 2009

Spiropyran-doped organic-inorganic hybrid coatings were prepared starting from glycidoxypropyl triethoxysilane and vinyltriethoxysilane by a sol-gel method. They were applied as a thin layer to polycarbonate sheets and their photochromic properties were investigated. The effect of polarity of solvents dissolving the spiropyran was investigated on the photochromic properties. The decoloration rate of the spiropyran decreased with increasing the polarity of solvents dissolving the spiropyran because the open form of the spiropyran was easily stabilized in the polar gel matrix.

• Korean Chemical Engineering Research
• /
• v.52 no.3
• /
• pp.388-394
• /
• 2014

Inorganic-organic hybrid coating solutions were synthesized using titania sol from titanium isopropoxide (TTIP) as an inorganic component and mixture of two or three types of silane coupling agents, such as methacryloxypropyl trimethoxysilane (MPTMS), aminopropyl triethoxysilane (APS), glycidoxypropyl trimethoxysilane (GPTMS) and vinyltriethoxysilane (VTES) as an organic component. The hard coating films were obtained by spin-coating on the polycarbonate sheets and curing the inorganic-organic hybrid coating solutions. The coating films made from the mixture of two types of silane coupling agents showed poor pencil hardness and adhesion, while those from the mixture of three types of silane coupling agents exhibited an improved pencil hardness of 2H~4H and adhesion of 5B. The refractive indexes of coating films were increased from 1.56 to 1.63 at 550 nm by increasing the content of titania sols from 20 to 30 g.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.18 no.3
• /
• pp.410-418
• /
• 1994

다양한 유기관능기를 가진 Silane가요제의 기능 양면성과 독특한 화학적 구조는 이들이 면섬유의 물성을 향상시키기 위한 in-situ 중합 및 가교처리의 단량체로 사용될 수 있는 가능성을 시사하므로, 본 연구에서는 이를 위한 기초 실험으로 수용액 상의 silane 단량체의 거동과 in-situ중합의 가능성을 조사하였다. 관능기를 달리하는 methyltriethoxysilane (MES), vinyltriethoxysilane (VES), vinyltriacetoxysilane (VAS)과 epoxy (glycidoxy) propyltrimethoxysilane (EMS) 등이 silane단량체로 선택되었다. Silane수용액의 안정성과 용해도는 단량체의 농도가 증가함에 따라 감소하였으며, pH에 의해서도 크게 영향을 받아 PH 3과 4.5사이에서 가장 안정함을 나타내었다. 10분간의 중기 고착과정에 의해서 충분한 양의 단량체가 면섬유 안으로 확산되었으며, 섬유의 방추성은 반응성이 높은 organotin촉매제를 사용하여 열처리한 후 증가되었다.

• Journal of the Korean Magnetic Resonance Society
• /
• v.6 no.2
• /
• pp.103-112
• /
• 2002

The photoproduced cation radical of N-methylphenothiazine $(PC_1)$ doped into phenyltriehtoxysilane (PhiTEOS), vinyltriethoxysilane (VTEOS) and methyltriethoxysilane (METOS) was studied with electron spin resonance (ESR) and electron nuclear double resonance (ENDOR). The photoinduced charge separation efficiency was determined by integration of ESR spectra which correspond to the amount of photoproduced cation radical in the matrices. This was correlatively studied with the polarity and pore size of the gel matrices. The relative polarity of the matrices was determined by measuring ${\lambda}_{max}$ values of $PC_1$ in the different matrices. The relative pore size among the matrices was determined by measuring relative proton matrix ENDOR line widths of the photoproduced cation of $PC_1$. The decay kinetic constants of the cation radical of $PC_1$ in the different matrices with relatively studied with fitting the biexponential decay curves after exposure at the ambient condition. This is correlatively interpreted with the polarity and pore size of the matrices.

• Elastomers and Composites
• /
• v.25 no.4
• /
• pp.273-279
• /
• 1990

The graft polymerization of 2-hydroxyethylmethacrylate(HEMA) and vinyltriethoxysilane(VTES) onto styrene-butadiene-styrene block copolymer(SBS) was carried out in toluene, with radical initiator such as benzoyl peroxide(BPO) and 2, 2'-azo-bis-isobutyronitrile(AIBIN) under nitrogen atmosphere. The degree of grafting was increased with the increases of the reaction temperature and time. And the effeciency of BPO was superior to that of AIBN. The mechanical properties and molecular weight of graft products were measured and the applicability as adhesive of plasticized PVC leather was examined.

• Elastomers and Composites
• /
• v.26 no.2
• /
• pp.115-122
• /
• 1991

Polychloroprene rubber was moisture-cured after treating them with silane coupling agents such as 3-mercaptopropyltrimethoxysilane(MPS), 3-methacryloxypropyltrimethoxysilane(MAS) and vinyltriethoxysilane(VES), especially MPS. The cure reaction is composed of two steps. The first is the reaction between chlorine atoms of CR and silane coupling agents. The second is the formation of cross-links which are siloxane linkage. The linkage is formed by the condensation of silanol groups which are produced by the hydrolysis of alkoxysilyl groups. The first reaction was kinetically studied and the reactivity of CR to silane coupling agents was determined in previous literature. Crosslinking density and mechanical properties of the moisture-cured elastomer filled with silica or non-filled were studied and the feasibility of this cure system was discussed.