The photoconductive $CdGa_2Se_4$ layer was grown through the hot wall epitaxy method. From the photocurrent (PC) measurements, the three peaks in the PC spectra were associated with the band-to-band transitions. The PC intensities were observed to decrease with decreasing temperature. The valence-band splitting on $CdGa_2Se_4$ was also observed by means of the PC spectroscopy. The crystal field splitting and the spin orbit splitting turned out to be 0.1604 and 0.4179 eV at 10 K, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.347-351
• /
• 2003

A p-$CdIn_2Te_4$ single crystal has been grown by the Bridgman method without a seed crystal in a tree-stage vertical electric furnace. From photocurrent measurements, it was found that three peaks, A, B, and C, corresponded to an intrinsic transition due to the band-to-band transition from the valence band states ${\Gamma}_7(A),\;{\Gamma}_6(B),\;and\;{\Gamma}_7(C)$ to the conduction band state ${\Gamma}_6$, respectively. Also, the valence band splitting of the $CdIn_2Te_4$ crystal has been confirmed by photocurrent spectroscopy. The crystal field splitting and the spin orbit splitting were obtained to be 0.2360 and 0.1119 eV, respectively. Also, the temperature dependence of the band gap energy of the $CdIn_2Te_4$ crystal has been driven as the following equation of $E_g(T)\;=E_g(0)\;-\;(9.43\;{\times}\;10^{-3})T^2/(2676\;+\;T)$. In this equation, the Eg(0) was estimated to be 1.4750, 1.7110, and 1.8229 eV at the valence band state A, B, and C, respectively. The band gap energy of the p-$CdIn_2Te_4$ at room temperature was determined to be 1.2023 eV.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.121-122
• /
• 2006

Single crystal of $CdIn_2Te_4$ were grown by the Bridgman method without using seed crystals. From photocurrent measurements, its was found that three peaks, A, B, and C, correspond to the instrinsic transition from the valence band states of ${\Gamma}_7$(A), ${\Gamma}_6$(B), and ${\Gamma}_7$(C) to the conducton band states of ${\Gamma}_6$, respectively. Crystal field splitting and spin orbit splitting were found to be at 0.2360 eV and 0.1119 eV, respectively, from found to be photocurrent spectroscopy.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.267-270
• /
• 2004

A silver indium sulfide($AgInS_2$) epilayer was grown by the hot wall epitaxy method, which has not been reported in the literature. The grown $AgInS_2$ epilayer has found to be a chalcopyrite structure and evaluated to be high qualify crystal. From the photocurrent measurement in the temperature range from 30 K to 300 K, the two peaks of A and B were only observed, whereas the three peaks of A, B, and C were seen in the PC spectrum of 10 K. These peaks. are ascribed to the band-to-band transition. The valence band splitting of $AgInS_2$ was investigated by means of the photocurrent measurement. The crystal field splitting, $\ddot{A}cr$, and the spin orbit splitting, $\ddot{A}so$, have been obtained to be 0.150 eV and 0.009 eV at 10 K, respectively. And, the energy band gap at room temperature has been determined to be 1.868 eV. Also, the temperature dependence of the energy band gap, $E_g(T)$, was determined.

• 센서학회지
• /
• 제15권6호
• /
• pp.397-405
• /
• 2006

Single crystal $AgGaSe_{2}$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $420^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $AgGaSe_{2}$ source at $630^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $AgGaSe_{2}$ thin films measured with Hall effect by van der Pauw method are $4.05{\times}10^{16}/cm^{3}$, $139cm^{2}/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $AgGaSe_{2}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}(T)$=1.9501 eV-($8.79{\times}10^{-4}{\;}eV/K)T^{2}$/(T+250 K). The crystal field and the spin-orbit splitting energies for the valence band of the $AgGaSe_{2}$ have been estimated to be 0.3132 eV and 0.3725 eV at 10 K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}So$ definitely exists in the ${\Gamma}_{5}$ states of the valence band of the $AgGaSe_{2}$. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1}-$, $B_{1}-$, and $C_{1}-$exciton peaks for n=1.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.234-238
• /
• 2004

A stoichiometric mixture of evaporating materials for $CuInSe_2$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $CuInSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were $620^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuInSe_2$ single crystal thin films measured with Hall effect by van der Pauw method are $9.62{\times}10^{l6}\;cm^{-3}$ and $296\;cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuInSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;=\;1.1851\;eV\;-\;(8.99{\times}10^{-4}\;eV/K)T^2/(T+153K)$. The crystal field and the spin-orbit splitting energies for the valence band of the $CuInSe_2$ have been estimated to be 0.0087 eV and 0.2329 eV at 10K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}_{so}$ definitely exists in the $\Gamma_6$ states of the valence band of the $CuInSe_2$. The three photocurrent peaks observed at 10K are ascribed to the $A_1-$, $B_1-$, and $C_1$-exciton peaks for n = 1.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.84-85
• /
• 2009

The single crystals of p-$CdIn_2Te_4$ were grown by the Bridgman method without the seed crystal. From photocurrent measurements, it was found that three peaks, A, B, and C, correspond to the intrinsic transition from the valence band states of $\Gamma_7(A)$, $\Gamma_6(B)$, and $\Gamma_7(C)$ to the conduction band state of $\Gamma_6$, respectively. The crystal field splitting and the spin orbit splitting were found to be 0.2360 and 0.1119 eV, respectively, from the photocurrent spectroscopy. The temperature dependence of the $CdIn_2Te_4$ band gap energy was given by the equation of $E_g(T)=E_g(0)$ - $(9.43\times10^{-3})T^2$/(2676+T). $E_g(0)$ was estimated to be 1.4750, 1.7110, and 1.8229 eV at the valence band states of A, B, and C, respectively. The band gap energy of $p-CdIn_2Te_4$ at room temperature was determined to be 1.2023 eV.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 제4회 영호남학술대회 논문집
• /
• pp.92-96
• /
• 2002

Hot wall epitaxy 방법을 이용하여 chalcopyrite 구조를 가진 고품질의 $AgInS_{2}$ 박막을 성장 하였다. 광전류 스펙트럼을 측정한 결과， 30K에서 300K까지는 단지 A 와 B 두개의 봉우리가 관측되었고 반면에 10K에서는 A,B,C 세 개의 봉우리가 관측되었다. 이때 이들 봉우리들은 band-to-band 전이에 기인하는 것으로 관측되었다. 광전류 측정으로부터 $AgInS_{2}$의 가전자대 갈라짐이 측정되었고 이로부터 10k에서 결정장에 의한 갈라짐 $D_{cr}$과 스핀궤도에 의한 갈라짐 $D_{so}$은 각각 0.150eV와 0.009eV로 관측되었다. 또한 에너지 밴드갭의 온도 의존성 $E_{g}(T)$에 대하여 연구하였고 성장된 $AgInS_{2}$ 박막의 에너지 밴드갭은 1.868eV 임을 알았다.

• 한국재료학회지
• /
• 제12권7호
• /
• pp.587-590
• /
• 2002

A silver indium sulfide ($AgInS_2$) epilayer was grown by the hot wall epitaxy method, which has not been reported in the literature. The grown $AgInS_2$ epilayer has found to be a chalcopyrite structure and evaluated to be high quality crystal. From the photocurrent measurement in the temperature range from 30 K to 300 K, the two peaks of A and B were only observed, whereas the three peaks of A, B, and C were seen in the PC spectrum of 10 K. These peaks are ascribed to the band-to-band transition. The valence band splitting of $AgInS_2$ was investigated by means of the photocurrent measurement. The crystal field splitting, $\Delta_{cr}$ , and the spin orbit splitting, $\Delta_{so}$ , have been obtained to be 0.150 eV and 0.009 eV at 10 K, respectively. And, the energy band gap at room temperature has been determined to be 1.868 eV. Also, the temperature dependence of the energy band gap, $E_{g}$(T), was determined.d.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.79-80
• /
• 2006

A stoichiometric mixture of evaporating materials for $CdIn_2S_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $CdIn_2S_4$ mixed crystal was deposited on thoroughly etched semi-Insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The temperature dependence of the energy band gap of the $CdIn_2S_4$ obtained from the absorption spectra was well described by the Varshni's relation. $E_g(T)=2.7116 eV-(7.74{\times}10^{-4} eV)T^2/(T+434)$. The crystal field and the spin-orbit splitting energies for the valence band of the $CdIn_2S_4$ have been estimated to be 0.1291 eV and 0.0248 eV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $AgInS_2$/GaAs epilayer. The three photocurrent peaks observed at 10K are ascribed to the $A_1-$, $B_1-$, and C1-exciton peaks for n = 1.