• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08a
• /
• pp.320-323
• /
• 2007

The vacuum sealing method is adopted to minimize the residual impurity gas by enhancing a base vacuum level, and the resultant changes in the reset, address, and sustain discharge characteristics, such as a firing voltage, IR emission, and ICCD image, were examined in comparison with the conventional sealing method in the 42-in. AC-PDP. In the PDP cells fabricated by the vacuum sealing method, the ICCD observation illustrates that the discharge is initiated and extinguished very fast and its IR emission intensity is high.

• Journal of Information Display
• /
• v.9 no.4
• /
• pp.39-44
• /
• 2008

This paper investigates the effects of the existing sealing methods, such as the conventional atmospheric-pressure sealing method and vacuum sealing, on temporal bright-image sticking. To produce a residual image caused by temporal brightimage sticking, the entire region of a 42-in panel with an Xe-(11%)-He(35%) gas mixture was abruptly changed to a full-white background image after displaying a square-type image at peak luminance for about 60s. From the monitoring of the difference in the display luminance, infrared emission, color temperature, and disappearing time between the cells with and without temporal bright-image sticking, it was observed that the vacuum sealing method contributes to the reduction of temporal bright-image sticking.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.703-706
• /
• 2004

This paper deals with the various sealing conditions in a vacuum and the discharge characteristics. The MgO thin film is prepared by e-beam evaporation method. Sealing process was performed in a vacuum at panel temperature of 430 $^{\circ}C$. We find the cracks on the MgO film surface, which results in higher discharge voltage and lower luminous efficiency. The vacuum in-line sealing technology does not require additional annealing process but induces the MgO cracks because of the high temperature sealing cycle in a vacuum. Therefore we modify the vacuum in-line sealing cycle which the MgO cracks are not found and the good characteristics of plasma displays are found in higher sealing pressure at sealing temperature of 430 $^{\circ}C$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08b
• /
• pp.1688-1691
• /
• 2007

This paper shows that the boundary image sticking can be prohibited completely by using the vacuum sealing process, which means that the residual impurities such as nitrogen or oxygen can be a critical factor inducing the boundary image sticking. The production of boundary image sticking was checked in the test panel fabricated by the $N_2$ or $O_2$ flow during the vacuum sealing process. As a result, the boundary image sticking did not appear in the case of $N_2flow$, whereas the boundary image sticking was observed in the case of $O_2$ flow even though the test panel was fabricated by the vacuum sealing process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.3
• /
• pp.181-185
• /
• 2016

One of the important issues for fabricating the microelectronic display devices such as FED, PDP, and VFD is to obtain a high vacuum level inside the panel. In addition, sustaining the initial high vacuum level permanently is also very important. In the conventional packing technology using a tabulation method, it is not possible to obtain a satisfiable vacuum level for a proper operation. In case of FED, the poor vacuum level results in the increase of operating voltage for electron emission from field emitter tips and an arcing problem, resultantly shortening a life time. Furthermore, the reduction of a sealing process time in the PDP production is very important in respect of commercial product. The most probable method for obtaining the initial high vacuum level inside the space with such a miniature and complex geometry is a vacuum in-line sealing which seals two glass plates within a high vacuum chamber. The critical solution for the vacuum sealing is to develop a frit glass to avoid the bubbling or crack problems during the sealing process at high temperature of about $400^{\circ}C$ under the vacuum environment. In this study, the suitable frit power was developed using a mixture of vitreous and crystalline type frit powders, and a vacuum sealed CNT FED with 2 inch diagonal size was fabricated and successfully operated.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.3
• /
• pp.961-966
• /
• 2012

The concern about vacuum glass is enhanced as society gets greener and becomes more concerned about energy savings due to the rising cost of oil. The glass edge sealing process needs the high reliability among the main process for the vacuum glass development in order to maintain between the two glass by the vacuum. In this paper, the process of the edge sealing was performed by using the hydrogen mixture gas which is the high density heat source unlike the traditional method glass edge sealing by using the frit as the soldering process. The ambient temperature in the electric furnace was set in the edge sealing to prevents the thermal impact and transformation of the glasses and the temperature distribution uniformity was measured. The parameter of the edge sealing was set through the basic test and the mathematical relation with the area of the glass edge parts according to the parameter was drawn using the multiple regression analysis method.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.1
• /
• pp.40-45
• /
• 2012

The glass edge sealing is one of the vacuum glazing core manufacturing process and it needs the high reliability for the vacuum keeping. Conventionally, the glass edge sealing had been being researched by the method that pasted the flit on the glass edge part and bonded two sheets of glass. But this way has the defect that can't make tempered glass. In order to remedy it's faults, in this paper, the glass edge was sealed by using the hydrogen mixture gas torch within the furnace. The parameter having an effect on the glass edge sealing through the basic test was set. And the correlation of the thickness of the glass edge and parameter were analyzed through the design of experiment. By using the Taguchi method, the optimal process condition for the glass edge sealing was drawn and the validity was verified.

• Korean Journal of Plant Resources
• /
• v.19 no.3
• /
• pp.436-439
• /
• 2006

This study was carried out to obtain basic information for optimum storage method of leaf, stem and root of Angelica acutiloba Radix, which is being utilized as major cultivated herbal medicine materials, root of Angelica acutiloba was stored for 3 months in different packing materials and sealing methods, such as punched packing, sealing and vacuum packing. The results are summarized as follows. The loss in weight as influenced by packing materials and sealing degree was the lowest at vacuum packing and complete sealing condition with transparent polyethylene film. The ratio of root rot during the storage period was not significantly different between polyethylene films, but it was significantly different between sealing conditions. Therefore, vacuum packing and complete sealing with polyethylene film are desirable storage condition for Angelica acutiloba Radix.

• Journal of Information Display
• /
• v.5 no.4
• /
• pp.7-11
• /
• 2004

Effects of base vacuum level on the electrical and optical characteristics of the plasma display panel (PDP) were investigated. The relationship between efficiency and base vacuum level before filling discharge gas was analyzed. For the base vacuum level of $1{\times}10^{-4}$ torr, firing voltage of a 2-inch diagonal PDP panel was 232 V at the discharge gas pressure of 400 torr and luminous efficiency was 1.5 lm/W at 180V sustaining pulse. On the other hand for $1{\times}10^{-6}$torr, the firing voltage was reduced to 215 V and luminous efficiency was improved considerably to 2.5 lm/W. We successfully demonstrated the smooth operation of tip-less PDP fabricated using vacuum in-line sealing method.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.05a
• /
• pp.709-710
• /
• 2012