• Journal of the Korean Applied Science and Technology
• /
• v.27 no.2
• /
• pp.188-195
• /
• 2010

In this study, we experimented that how to synthesis waterborne urethane-acrylic hybrid resin for leather coatings. First of all, We had analyzed data by FT-IR, SEM and TGA for the machanical properties. By TGA analysis polymers showed heat distortion temperature. and by FT-IR measurement we confirmed that synthesis of urethane and acrylic. In the experiment, solvent resistance, polyurethane and acrylic grades 4-5 showed both a high. Tensile strength measured in the waterborne polyurethane > Acrylic emulsion showed strength in the order. Films were obtained by coating the water born resin on leveled surfaces and allowing them to dry at room temperature for 72hrs. After demolding, the films were kept in a desiccator to avoid moisture contant at $25^{\circ}C$ for 45hrs before the measurements. In this result, the mechanical propersies of waterborne polyurethane-acrylic hybrid resin showed that how effect to resin in leather coating between polyurethane content and acrylic content. Therefore, acrylic emulsion had most high solvent resistance glade and waterborne polyurethane had good result in abrasion test and tensile strength.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.2
• /
• pp.203-212
• /
• 2011

In this study we experimented that how chain extension influences to waterborne urethane-acrylic hybrid resin for leather garment coatings. We knew that polyurethane-acrylic hybrid resins had 5 grades of solvent resistance. Tensile strength measured in the polyurethane-acrylic resin(EDA 5.37 g, 1.928 kgf/$mm^2$) had the most strong strength. Also polyurethane-acylic hybrid resin(EDA 5.37 g. 30.2 mg. loss) had better result than other hybrid resins. EDA contents higher, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-acrylic hybrid resin showed the effect in leather coating with ratio of EDA.

• Journal of Adhesion and Interface
• /
• v.8 no.1
• /
• pp.8-14
• /
• 2007

Poly(urethane-methyl methacrylate) hybrid emulsions can be controlled with their thermal, mechanical and anti-chemical properties as plastic coating materials. In this study, water dispersed poly(urethane-methyl methacrylate) hybrid emulsions were prepared by prepolymer synthesis and soap free emulsion polymerization. For imparting hydrophilicity on polyurethane prepolymer, 2,2-bis (hydroxymethyl) propionic acid was added to the polyurethane prepolymer with methyl methacrylate monomer and was neutralizated by triethylamine (TEA). After neutralization, the prepolymer mixture was dispersed in the water phase with stable droplets. The synthesis was carried out with chain extension from the ethylene diamine and initiation of methyl methacrylate by soap free emulsion polymerization. Stable poly(urethane-methyl methacrylate) hybrid emulsion was successfully obtained with different synthetic conditions and acrylic monomer contents. Poly(urethane-methyl methacrylate) hybrid emulsion were characterized and compared with tensile strength, viscosity, and adhesion properties.