• 한국응용과학기술학회지
• /
• 제27권2호
• /
• pp.188-195
• /
• 2010

In this study, we experimented that how to synthesis waterborne urethane-acrylic hybrid resin for leather coatings. First of all, We had analyzed data by FT-IR, SEM and TGA for the machanical properties. By TGA analysis polymers showed heat distortion temperature. and by FT-IR measurement we confirmed that synthesis of urethane and acrylic. In the experiment, solvent resistance, polyurethane and acrylic grades 4-5 showed both a high. Tensile strength measured in the waterborne polyurethane > Acrylic emulsion showed strength in the order. Films were obtained by coating the water born resin on leveled surfaces and allowing them to dry at room temperature for 72hrs. After demolding, the films were kept in a desiccator to avoid moisture contant at $25^{\circ}C$ for 45hrs before the measurements. In this result, the mechanical propersies of waterborne polyurethane-acrylic hybrid resin showed that how effect to resin in leather coating between polyurethane content and acrylic content. Therefore, acrylic emulsion had most high solvent resistance glade and waterborne polyurethane had good result in abrasion test and tensile strength.

• 한국응용과학기술학회지
• /
• 제28권2호
• /
• pp.203-212
• /
• 2011

In this study we experimented that how chain extension influences to waterborne urethane-acrylic hybrid resin for leather garment coatings. We knew that polyurethane-acrylic hybrid resins had 5 grades of solvent resistance. Tensile strength measured in the polyurethane-acrylic resin(EDA 5.37 g, 1.928 kgf/$mm^2$) had the most strong strength. Also polyurethane-acylic hybrid resin(EDA 5.37 g. 30.2 mg. loss) had better result than other hybrid resins. EDA contents higher, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-acrylic hybrid resin showed the effect in leather coating with ratio of EDA.

• 접착 및 계면
• /
• 제8권1호
• /
• pp.8-14
• /
• 2007

폴리우레탄에 아크릴기가 도입된 poly(urethane-methyl methacrylate) 혼성 에멀젼 코팅 수지는 플라스틱 코팅 수지로써 열적, 기계적 물성 및 내화학성을 제어할 수 있다. 이에 본 연구에서는 프리폴리머 혼합 공정과 무유화 중합 방법을 이용하여 수분산된 poly(urethane-methyl methacrylate) 혼성 에멀젼을 합성하였다. 즉, 폴리우레탄 프리폴리머 합성 단계에서 2,2-bis (hydroxymethyl) propionic acid (DMPA)을 투입하고 methyl methacrylate (MMA) 단량체를 투입한 후, triethylamine (TEA)을 이용하여 DMPA의 카르복실기를 중화시켜 친수성기를 도입하였다. 이를 수분산시켜 안정한 액적을 형성시킨 후, 사슬연장 및 무유화 중합 방법에 의해 합성반응을 진행하였다. 이때 제조공정 조건 및 아크릴계 단량체의 함량을 달리하여 poly(urethane-methyl methacrylate) 혼성 에멀젼의 다양한 샘플을 얻으며, 수분산 샘플의 물성(인장강도, 점도, 부착성 등) 및 코팅필름의 특성을 평가 비교하였다.