• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.288-291
• /
• 2004

In this paper, to make ultra-high strength SFRCC with the range of compressive strength 180MPa, it was investigated the constitute factors of ultra-high strength SFRCC influenced on the compressive strength. The experimental variables were water-cementitious ratio, replacement of silica fume, size and proportion of sand, type and replacement of filling powder, and using of steel fiber in ultra-high strength SFRCC. As a result, in water-binder ratio 0.18, we could make ultra-high strength SFRCC with compressive strength 180MPa through using of silica fume, quartz sand with below 0.5mm, filling powder and steel fiber.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.373-376
• /
• 2008

Ultra High Strength Concrete(UHSC) is necessary a clear presentation about mechanical property that is different from normal strength concrete and an evaluation of serviceability of high rise building which is used ultra high strength concrete. To mixing ultra high strength concrete with $f_{ck}$=150MPa pre-mix cement were manufactured and experimental study were conducted to evaluated on the mixing properties and compressive strength with major variables as unit cement contents, water-binder ratio and type of pre-mix cement. As a test result, it is shown that the concrete mixing time is required about 5$^{\sim}$6 minute untill the each materials(ordinary portland cement, silica fume, blast-furnace slag powder and anhydrite) are revitalized enough. A slump flow of fresh concrete are shown about 700$^{\sim}$750mm with proper viscosity. And average value of concrete compressive strength are shown about 77% in 7days, 87% in 14days and 102% in 56days for 28days of concrete material age. From this experimental study, a proper mixture proportion of pre-mix cement are recommended about 54$^{\sim}$59% OPC, 25$^{\sim}$30% blast-furnace slag powder and 10$^{\sim}$15% silica fume for mix the ultra high strength concrete with $f_{ck}$=150MPa.

• Structural Engineering and Mechanics
• /
• v.37 no.1
• /
• pp.1-15
• /
• 2011

The response of concrete to transient dynamic loading has received extensive attention for both civil and military applications. Accordingly, thoroughly understanding the response and failure modes of concrete subjected to impact or explosive loading is vital to the protection provided by fortifications. Reactive powder concrete (RPC), as developed by Richard and Cheyrezy (1995) in recent years, is a unique mixture that is cured such that it has an ultra-high compressive strength. In this work, the concrete cylinders with different steel fiber volume fractions were subjected to repeated impact loading by a split Hopkinson Pressure Bar (SHPB) device. Experimental results indicate that the ability of repeated impact resistance of ultra-high-strength concrete was markedly superior to that of other specimens. Additionally, the rate of damage was decelerated and the energy absorption of ultra-high-strength concrete improved as the steel fiber volume fraction increased.

• Advances in concrete construction
• /
• v.8 no.1
• /
• pp.21-31
• /
• 2019

The rich recipe of ultra high performance concrete (UHPC) offers the higher mechanical, durability and dense microstructure property. The variable like cement/sand ratio, amount of supplementary cementitious material, water/binder ratio, amount of fiber etc. alters the UHPC hardened properties to any extent. Therefore, to understand the effects of these variables on the performance of UHPC, inevitably a stage-wise development is required. In the present experimental study, the effect of sand/cement ratio, the addition of finer material (fly ash and quartz powder) and, hybrid fiber on the fresh, compressive and microstructural property of UHPC is evaluated. The experiment is conducted in three phases; the first phase evaluates the flow value and strength attainment of ingredients, the second phase evaluates the efficiency of finer materials (fly ash and quartz powder) to develop the UHPC and the third phase evaluate the effect of hybrid fiber on the flow value and strength of ultra high performance hybrid fiber reinforced concrete (UHP-HFRC). It has been seen that the addition of fly ash improves the flow value and compressive strength of UHPC as compared to quartz powder. Further, the usage of hybrid fiber in fly ash contained matrix decreases the flow value and improves the strength of the UHP-HFRC matrix. The dense interface between matrix and fiber and, a higher amount of calcium silicate hydrate (CSH) in fly ash contained UHP-HFRC is revealed by SEM and XRD respectively. The dense interface (bond between the fiber and the UHPC matrix) and the higher CSH formation are the reason for the improvement in the compressive strength of fly ash based UHP-HFRC. The differential thermal analysis (DTA/TGA) shows the similar type of mass loss pattern, however, the amount of mass loss differs in fly ash and quartz powder contained UHP-HFRC.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.441-444
• /
• 2008

Ultra high performance concrete (UHPC) in this study is composed of sand, cement, silica fume, siliceous powder, superplasticizer and steel fiber. UHPC is composed of fine mineral particles below 0.5mm in diameter. In general, siliceous powder improves the mechanical properties of concrete by physical and chemical effect. Physical effect is related with filling interior voids which weaken the mechanical properties and chemical effect with reaction of $SiO_2$ with cement hydrates in a condition of high temperature and pressure. We evaluated the effect of siliceous powder's particle size on the mechanical properties of ultra high performance concrete in air pressure and $90^{\circ}C$ steam curing condition. siliceous powder's particle size in this study is in the range of $2{\mu}m$ to $26{\mu}m$. Fluidity in a fresh concrete, compressive strength, ultimate strain, elastic modulus and flexural strength in a hardened concrete was evaluated. We could find out that the smaller siliceous powder's particle size is, the better the fluidity and strength properties.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.6 s.58
• /
• pp.135-147
• /
• 2009

In order to develop the ultra high strength concrete over 400Mpa at 28 day, Low-heat portland cement, ferro-silicon, silica-fume and steel fiber were mixed and tested under the special autoclave curing conditions. Considering the influence of Ultra high strength concrete. normal concrete is used as a comparison with low water-cement ratio possible Low-heat portland cement. Additionally, as a substitution of aggregates, we analyzed the compressive strength of Ferro Silicon by making the states of mixed and curing conditions differently. In addition, SEM films testified the development of C-S-H hydrates of Type III & Type IV, and tobermolite, zonolite due to the high temperature, high pressure of autoclave curing. Fineness of aggregate, filler and reactive materials in concrete caused 420Mpa compressive strength at 28day successfully.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.5
• /
• pp.547-558
• /
• 2023

This research delves into the fabrication of an ultra-high-strength concrete, enriched with oxidized graphene nanoplatelet(GO) and hollow glass powder(HGP), notably eschewing the conventional inclusion of silica fume(SF). The primary objective was to scrutinize the autogenous shrinkage characteristics of this innovative formulation. It was discerned that the NewMix specimen, which incorporated the cGO(sourced from Company C) and HGP, and intentionally bypassed SF, showcased a commendable 13% reduction in autogenous shrinkage relative to the benchmark(Ref) specimenthat incorporated SF. Moreover, the proclivity for crack formation owing to autogenous shrinkage in the NewMix was observed to manifested by NewMix at the juncture of cracking emerged as the apex value. Attributed to the expansive specific surface area and exemplary dispersibility of cGO, it was postulated that the concrete's pore structure benefitted from enhanced infill, leading to a reduction in autogenous shrinkage. Additionally, the cGO integration fortified the concrete's resistance to crack initiation. Consequently, such an enhancement is posied to be pivotal in mitigating crack propagation resulting from autogenous shrinkage in ultra-high-strength concrete.

• Journal of the Korea Concrete Institute
• /
• v.22 no.3
• /
• pp.287-295
• /
• 2010

In this study, ordinary Portland cement was used and the air void was minimized by using minute quartz as the filler. In addition, steel fibers were used to mitigate the brittle failure problem associated with high strength concrete. This study is in progress to make an Ultra-high strength powdered concrete (UHSPC) which has compressive strength over 300 MPa. To increase the strength of concrete, we have compared and analyzed the compressive strengths of the concretes with different mix proportions and curing conditions by selecting quartz sand, dolomite, bauxite, ferro silicon which have diameters less than 0.6 mm and can increase the bond strength of the transition zone. Ultra-high strength powdered concrete, which is different from conventional concrete, is highly influenced by the materials in the mix. In the study, the highest compressive strength of the powdered concrete was obtained when it is prepared with ferro silicon, followed in order by Bauxite, Dolomite, and Quartz sand. The amount of ferro silicon, when the highest strength was obtained, was 110%, of the weight of the cement. SEM analysis of the UHSPC showed that significant formation of C-S-H and Tobermorite due to high temperature and pressure curing. Production of Ultrahigh strength powdered concrete which has 28-day compressive strength upto 341MPa has been successfully achieved by the following factors; steel fiber reinforcement, fine particled aggregates, and the filling powder to minimize the void space, and the reactive materials.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.399-402
• /
• 2005

In ultra-high strength SFRCC(Steel Fiber Reinforced Cementious Composites), much silica fume are used to improve strength, flowability and durability. Silica fume have merits of filling the voids, enhancement of reheological chracteristics, production of secondary hydrates by pozzolanic reaction in reactive powder concretes. However silica fume has been imported in high-cost in domestic industry, we need to investigate replaceable material in stead of silica fume in a view of economy Therefore, in this paper, in order to investigate replacement of silica fume in ultra-high strength SFRCC we used the granulate blast-furnce slag with finess 4000, 6000, 8000. As a results, we have evaluated that the bigger the finess the more increase compressive strength of ultra-high strength SFRCC using the blast-furnce slag and there was no problem from the viewpoint of flowability and compressive strength when we use blast-furnce $50\%$ with replacement ratio of silica fume

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.04a
• /
• pp.79-88
• /
• 1993

The purpose of this study is to provide a firm base for the quality improvement of high strength concrete and the development of ultra high strength concrete as well as enviromental con-servation and utilization of byproducts from industrial processing such as Fly ash and Silica fume. A comprehensive experimental study was performed to investigate the effects on the quality improvement of high strength concrete using mineral admixtures. As results, 400~500kg/$\textrm{cm}^2$ compressive strength and excellent flowability can be obtained if fly ash is replaced with cement in the range of 305. In case of using powder type silica fume, 600~700 kg/$\textrm{cm}^2$ compressive strength is showed and 600~800kg/$\textrm{cm}^2$ compressive strength cam be obtained with liquid type silica fume. But it is necessary to increase dosage of high range water reducer for flowability using powder type silica fume. Especially, higher strength concrete cam be obtained when maximum size of coarse aggregate is lower than 25mm.