• 한국산림과학회지
• /
• 제56권1호
• /
• pp.77-81
• /
• 1982

4수종(樹種) 열대산활엽수재(熱帯産闊葉樹材) Xylan의 성상(性状)을 분석(分析)하였다. Xylan은 24% KOH로 추출(抽出)하였으며 ethanol 적하법(適下法)으로 정제(精製)하고, Uronic acid잔기(残基), methoxyl기(基) 및 acetyl기(基)의 함유량(含有量)과 점도법(粘度法)에 의하여 중합도(重合度)를 측정(測定)하였다. Uronic acid잔기(残基)에 대한 Xylan잔기(残基)의 비(比)는 Xylan함유율(含有率)이 온대산활엽수재(温帯産闊葉樹材)의 그것과 비슷한 mangrove재(材)의 경우만이 온대산활엽수재(温帯産闊葉樹材)의 그것과 필적(匹敵)하는 높은 값을 나타내었다. Methoxyl기(基)도 Uronic acid잔기(残基) 함유량(含有量)의 결과(結果)와 동일(同一)하였다. DMSO추출(抽出) Xylan중(中)에는 D-xylose잔기(残基)이외의 Hemicellulose도 다수(多数) 함유(含有)되어 있으며, acetyl기량(基量)은 MDX 5.4%, RDX 6.8%로 xylose 잔기(残基) 5~6개당(個当) 1개(個)이고, DMSO추출(抽出) 된지 않은 Xylan에는 acetyl기(基)가 존재(存在)하였다. 점도법(粘度法)에서 측정(測定)한 $\bar{P}_n$는 200전후(前後)로 온대산활엽수재(温帯産闊葉樹材)와 비슷하였고, Uronic acid잔기(残基)로 계산(計算)한 $\bar{DP}n$ 열대산활엽수재(熱帯産闊葉樹材)와 비슷하였다.

• Journal of Forest and Environmental Science
• /
• 제36권3호
• /
• pp.225-232
• /
• 2020

Chemical modification of wood is an effective method to enhance the biological durability of wood with no toxic effect on the environment. In this study, wood of Triplochiton scleroxylon was modified using acetylation techniques. A total of one hundred wood blocks, (each 20×20×60 mm) obtained from a 22-year old T. scleroxylon tree were conditioned and acetylated at 120℃ in a bioreactor containing acetic anhydride for 60, 120, 180, 240 and 300 minutes. The percentage weight gain of acetylated wood was determined. The untreated (control) and treated blocks were exposed to Pleurotus ostreatus (white rot fungus) and Fibroporia vaillanti (brown rot fungus) after which moisture content (MC) and weight loss (WL) was monitored for 16 weeks. Data were analysed using descriptive and inferential statistics at p<0.05 level of significance. The percentage weight gain of acetylated wood samples increased with time from 10.4% (60 minutes) to 22.7% (300 minutes). MC of untreated blocks inoculated with Pleurotus ostreatus was significantly higher than those of Fibroporia vaillantii after 16 weeks exposure. There was no significant difference in the MC of the of the acetylated samples for the two fungi after 300 minutes reaction time. The WL of untreated blocks inoculated with Fibroporia vaillantii was higher than those of Pleurotus ostreatus, however, the two fungi showed no significant difference in the WL for the acetylated samples after 16 weeks exposure. Acetylation prevents moisture absorption and inhibition of fungi growth in acetylated wood compared to untreated wood, thereby enhancing the durability of Triplochiton scleroxylon.

• Journal of the Korean Wood Science and Technology
• /
• 제42권6호
• /
• pp.635-645
• /
• 2014

최근 인도네시아에서 인공조림중인 8수종 목재자원의 효율적 이용방안 모색을 위해 해부학적 특성을 조사하였다. 침엽수종인 Damar와 Sumatran pine의 생장륜은 뚜렷하지 않았고 Sumatran pine은 수지구가 존재하였으나 Damar는 수지구가 관찰되지 않았다. Damar는 편백형과 삼나무형 벽공을 보였고, Sumatran pine은 창상벽공과 소나무형벽공의 분야벽공형태를 보였다. 두 수종 모두 $3,000{\mu}m$ 이하로 다소 짧은 가도관의 길이를 보였고, 방사조직은 주로 단열방사조직으로서 Sumatran pine의 경우 방추형 방사조직이 관찰되었다. 활엽수 수종은 모두 산공재였고 Afrika와 Simpur Batu는 고립관공, Angsana는 집단관공, Mahoni는 2~4열의 방사복합관공, Mindi와 Trembesi에서는 2~3열의 방사복합관공과 익상유조직, 연합익상유조직이 다른 수종에 비해 뚜렷하게 관찰되었다. Afrika, Mahoni와 Simpur Batu는 평복세포와 1~2열의 직립세포로 구성된 이성방사조직이, Angsana, Mindi와 Trembesi는 평복세포로 이루어진 동성방사조직이 관찰되었다. Simpur batu는 높이 1 mm를 초과하는 3~6열의 다열 방사조직 폭을 보였으며, 이외 5개 수종은 1~3열의 방사조직 폭을 보였다. 단위면적($mm^2$)당 관공의 수는 Angsana와 Simpur Batu가 다른 수종에 비해 많았으며 특히 Simpur Batu가 가장 많게 나타났다. 모든 수종의 목섬유길이는 수심부에서 수피로 갈수록 증가하는 경향을 보였으며, Simpur Batu가 가장 긴 섬유의 길이를, Angsana와 Trembesi가 가장 짧은 섬유길이를 나타냈다.

• Journal of the Korean Wood Science and Technology
• /
• 제34권2호
• /
• pp.68-77
• /
• 2006

The heartwood of cengal (Neobalanocarpus heimii) is known to have a high degree of decay resistance by virtue of its high extractive content. After 30 years in ground contact an utility pole of this tropical hardwood was found to be degraded only in the surface layers by cavity-forming soft rot fungi. The present work was undertaken 1) to characterize the degradation of cengal heartwood from the aspect of ultrastructure and chemistry and 2) to investigate the correlation between soft rot decay and its extractive microdistribution in wood tissues. The chemical analysis of cengal heartwood revealed the presence of a high amount of extractives as well as lignin. The wood contained a relatively high amount of condensed lignin and the guaiacyl units. Microscopic observations revealed that vessels, fibers and parenchyma cells (both ray and axial parenchyma) all contained extractives in their lumina, but in variable amounts. The lumina of fibers and most axial parenchyma were completely or almost completely filled with the extractives. TEM micrographs showed that cell walls were also impregnated with extractives and that pit membranes connecting parenchyma cells were well coated and impregnated with extractives. However, fungal hyphae were present in the extractive masses localized in cell lumina, and indications were that the extractives did not completely inhibit fungal growth. The extent of cell wall degradation varied with tissue types. The fibers appeared to be more susceptible to decay than vessels and parenchyma. Middle lamella was the only cell wall region which remained intact in all cell types which were severely degraded. The microscopic observations suggested a close correlation between extractive microdistribution and the pattern and extent of cell wall degradation. In addition to the toxicity to fungi, the physical constraint of the extractive material present in cengal heartwood cells is likely to have a profound effect on the growth and path of invasion of colonizing fungi, thus conferring protection to wood by restricting fungal entry into cell walls. The presence of relatively high amount of condensed lignin is also likely to be a factor in the resistance of cengal heartwood to soft rot decay.

• Journal of the Korean Wood Science and Technology
• /
• 제41권4호
• /
• pp.327-336
• /
• 2013

인도네시아에서 자생하는 수종인 White Jabon (Anthocephalus cadamba)과 Red Jabon (Anthocephalus macrophyllus)의 해부학적 특성을 IAWA 분류기준에 의거하여 조사 및 비교하였다. 두 수종은 산공재로서, 대부분 2~3열의 방사복합관공의 형태로 관찰되었다. 접선방향의 도관 직경은 $100{\sim}200{\mu}m$의 범위로, $mm^2$당 도관의 수는 5~20개의 범위로 분류되었고, White Jabon의 도관수가 더 많았다. 두 수종에서 $mm^2$당 고립관공의 수는 비슷했으나 복합관공은 White Jabon이 다소 많이 출현하였다. 두 수종의 횡단면에서 축방향유조직은 산재상의 형태를 보였으나, White Jabon은 그 출현빈도가 매우 낮았다. 방사단면에서 방사조직은 평복세포와 4열 이상의 직립세포로 구성된 형태가 주로 관찰되었으며, 부분적으로 직립동성형 방사조직이 관찰되었다. 접선단면상에서 White Jabon의 방사조직은 1~V3열, Red Jabon은 1~2열로 관찰되었으며, 방사조직의 높이는 White Jabon이 $420{\mu}m$, Red Jabon이 $474{\mu}m$로 나타났다. 목섬유의 평균 길이는 $900{\sim}1,600{\mu}m$의 범위였고, 수에서 수피부로 이행할수록 증가하는 방사방향 변이성을 나타냈다.

• 한국산림과학회지
• /
• 제35권1호
• /
• pp.24-32
• /
• 1977

아염소산염법(亞鹽素酸鹽法)에 의하여 대부분(大部分) 탈(脫) lignin된 holocellulose를 얻었다. Alkali농도별(濃度別)의 추출(抽出)에서는 5% KOH로 3회추출(回抽出)하여도 일부(一部)의 xylan이 잔존(殘存)하며 타(他)의 hemicellulose와 cellulose의 분해성물질(分解生成物)이 얻어지며, 10%와 24% KOH추출(抽出)은 그와 같이 좋은 결과(結果)가 얻어졌다. Xylan의 침전단리(沈澱單離)에 다량(多量)의 ethanol을 사용(使用)하는 상법(常法)보다는 약(約) 1/10로 농축(濃縮)하여 cellophane막(膜)에 의한 투석법(透析法)으로 소량(少量)의 ethanol이라도 회수율(回收率)과 높은 순도(純度)의 xylan이 얻어졌다. Glucornannan의 단리(單離)에 있어서 5% KOH 추출잔사(抽出殘査)는 xyJan함유량(含有量)이 많고 10%와 24% KOH 추출잔사(抽出殘査)는 그의 같은 결과(結果)이며, glucose와 mannose의 비(比)는 약(約) 1 : 1이다. Fehling용액정제(溶液精製)는 비교적(比較的) 순수(純粹)한 xylan을 얻지만, 분화분해(孵化分解), 조작(操作)의 번잡(煩雜) 및 회수율(回收率)이 낫고, 그다지 좋은 방법(方法)은 아니다. Ethanol적하법(滴下法)은 1일(日)정제(精製)라도 고수율(高收率) 및 고순도(高純度)의 xylan이 얻어지고 조작(操作)의 영역(容易)등을 고려(考慮)하여 대단히 우수한 xylan 정제법(精製法)이다. 그러나 양정제법(兩精製法)으로 arabinose잔기(殘基)를 완전(完全)히 제거(除去)할 수는 없었다. 이것은 후보(後報)에 검토(檢討)를 보고(報告)한다.