• Computers and Concrete
• /
• 제16권1호
• /
• pp.125-140
• /
• 2015

This paper describes the numerical calculation of elastic properties of a simulated microstructure of cement paste from very early age, when most previous models fail to give accurate results. The development of elastic properties of tricalcium silicate pastes was calculated by discretising a numerical resolution-free 3D vector microstructure to a regular cubic mesh. Due to the connections formed in the microstructure as an artefact of the meshing procedure, the simulated elastic moduli were found to be higher than expected. Furthermore, the percolation of the solids was found to occur even before hydration started. A procedure to remove these artefacts, on the basis of the information available in the vector microstructures was developed. After this correction, a better agreement of the experimental results with calculations was obtained between 20% and 40% hydration. However, percolation threshold was found to be delayed significantly. More realistic estimates of percolation threshold were obtained if either flocculation or a densification of calcium silicate hydrate with hydration was assumed.

• 대한소아치과학회지
• /
• 제28권4호
• /
• pp.700-708
• /
• 2001

소아환자에 있어 외상성 손상은 미완성된 치근의 발육을 방해할 수 있다. 미완성된 치아의치수가 괴사된 경우 근관은 완전히 세척되어져야 한다. 그러나 apical stop이 부족하고 얇고 부서지기 쉬운 치수벽 때문에 적절한 apical seal을 얻기 위해서는 치근단 형성술을 시행해야 한다. 지금까지 수산화 칼슘이 치근단 형성술의 선택약제가 되어왔다. 그러나, 수산화칼슘을 이용한 치근단 형성술은 치료시기가 다양하고, apical closure도 불확실하며, 환자 follow up이 어렵고, 치료가 늦어지는 한계가 있다. 이에 인공적인 apical barrier를 형성시켜 근관의 즉각적인 충전을 할 수 있는 MTA(Mineral Trioxide Aggregate, DENTSPLY Tulsa Dental, U.S.A)를 이용하였다. MTA는 tricalcium silicate, tricalcium aluminate, tricalcium oxide와 silicate oxide와 같은 친수성 입자로 구성된다. 또한 소량의 mineral oxide와 bismuth oxide powder를 포함한다. MTA는 경화후 pH가 수산화칼슘 또는 $Ca(OH)_2$와 유사한 12.5로 항균작용을 지닌다. 용해도가 낮고, 상아질보다 약간 더 큰 방사선 불투과성을 보인다. 또한 다른 재료들보다 미세누출이 상당히 적고 다른 재료들보다 경조직 형성 능력이 뛰어나다. 본 증례는 전북대학교 소아치과에 외상으로 인해 치근단이 미완성된 미성숙 영구치의 치근단 형성술을 위해 내원한 환아에 대해 MTA를 적용하여 양호한 결과를 얻었기에 이에 보고하는 바이다.

• 대한소아치과학회지
• /
• 제46권1호
• /
• pp.76-84
• /
• 2019

이 연구의 목적은 3종의 수복재료와 3종의 tricalcium-silicate 기반 치수복조제의 미세누출을 평가하고, 이들 치수복조제와 상아질 사이의 전단결합강도를 비교하는 것이다. 수복재료로는 복합레진(CR), 레진강화형 글래스아이오노머 시멘트(RMGI), 그리고 전통적인 글래스아이오노머 시멘트(GIC)를, 치수복조제로는 TheraCal $LC^{(R)}$(TLC), $Biodentine^{(R)}$ (BD), 그리고 $ProRoot^{(R)}$ white MTA (WMTA)을 사용했다. 소의 절치에 5급와동을 형성하여 이를 적용하는 치수복조제와 수복재료에 따라 9개의 그룹으로 분류하고 0.5% fuchsin 용액을 이용한 염색침투법을 시행했다. 각 표본을 절단하고 입체현미경으로 관찰해 미세누출 정도를 평가했다. 아크릴 레진에 소 절치의 임상적 치관을 매몰한 후 수평으로 절단해 준비한 표본을 임의로 3그룹으로 나누었다. 표본의 상아질에 그룹별로 TLC, BD, 그리고 WMTA 블록을 적용한 후 universal testing machine을 이용해 전단결합강도를 측정했다. 미세누출은 TLC + GIC, TLC + RMGI, TLC + CR, 그리고 BD + GIC 그룹에서 가장 적었고, WMTA + RMGI와 WMTA + CR 그룹에서 가장 많았다. 전단결합강도는 WMTA 그룹에서 다른 그룹보다 통계적으로 유의하게 낮은 것으로 나타났다.

• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1417-1422
• /
• 1994

Effect of MgO, CaSO4, and CaF2 addition on the formation of clinker minerals in portland cement have been investigated by measuring the amounts of free-CaO and C3S in the fired specimens and analyzing the Mg and S concentration in C3S and C2S. It was found that CaSO4 inhibited C3S formation but MgO addition offset this effect of CaSO4. MgO addition also enhanced the mineralizing effect of CaSO4+CaF2, resulting in the acceleration of C3S formation. It was suggested that Mg might inhibit the formation of sulphate compounds rim around C2S and thus C2S+CaOlongrightarrowC3S reaction was facilitated.

• 한국세라믹학회지
• /
• 제11권1호
• /
• pp.29-35
• /
• 1974

Effect of calcium sulfate and barium sulfate on the formation of portland cement clinker was studied by means of chemical analysis. DTA and X-ray diffraction analysis. In the presence of liquid phase, effect of the additives on the formation of tricalcium silicate was examined according to the reaction, 2CaO.$SiO_3$＋CaO$\longrightarrow$3CaO.$SiO_3$, which is the principal reaction in portland cement clinkerization, and optimum conditions in firing clinker concerning amount of additive, firing time and temperature were determined, and its kinetics was referred to. The experimental results are summerized as follow: (1) Appropriate burning temperature range of cement clinker is more limited as the content of calcium sulfate in clinker is increased. Amount of calcium sulfate, firing time and temperature in proper condition of clinkerization is related to each others. Being added suitable quantity of calcium sulfate, firing temperature of clinker can be lowered about $100^{\circ}C$. (2) When 3-5 mole% of calcium sulfate is added, firing time of 15-30 minutes at about $1380^{\circ}C$ is reasonable, and if the content is over7 mole %, firing for 1 hr. or more at $1350^{\circ}C$ is anticipated to be optimum condition. (3) In the reaction of tricalcium silicate formation, the role of barium sulfate as a mineralizer is similar to that of calcium sulfate, but the optimum firing temperature of cement clinker containing barium sulfate tends to be 20-$30^{\circ}C$ higher than that of clinker containing calcium sulfate. (4) When barium sulfate is used as mineralizer, 2-3 mole % of it to tricalcium silicate is recommended and if it is added more than this amount, free CaO is increased rapidly in clinker and alite formation is inhibited.

• 대한소아치과학회지
• /
• 제46권4호
• /
• pp.392-399
• /
• 2019

이 연구의 목적은 tricalcium silicate cement 중 하나인 TheraCal LC의 광중합 시간과 거리에 따른 중합도를 평가하는 것이었다. 금속주형을 이용해 시편을 제작하여 Vickers hardness number (VHN)를 측정하였으며, 중합시간과 조사시간에 따른 시편의 미세경도 값을 비교 분석하였다. 그 결과, 모든 군에서 상면의 VHN이 하면의 VHN보다 유의성 있게 컸다(p < 0.05). 하면의 VHN은 모든 중합거리에서 중합시간이 증가함에 따라 유의하게 증가하였고(p < 0.05), 중합시간이 일정하고 중합거리가 4.0 mm 이상이 되었을 때 유의하게 감소하였다(p < 0.05). 또한 시편을 20초간 중합한 경우 하면의 VHN은 2를 넘지 못했으며 이는 상면의 10%에 해당하였다. 이 연구 결과에 의하면, 모든 중합거리에서 TheraCal LC 시편의 하면까지 중합하기에 20초의 광중합 시간은 충분하지 않았으며, 중합도를 높이기 위해서 중합시간의 증가와 도포 두께의 감소를 고려해볼 필요가 있다.

• 대한소아치과학회지
• /
• 제43권2호
• /
• pp.137-144
• /
• 2016

이 연구의 목적은 다양한 산성 환경에서 규산 삼칼슘 재료인 Biodentine$^{(R)}$, Theracal$^{(R)}$, ProRoot MTA$^{(R)}$의 압출강도를 측정하고 표면형태를 관찰하는 것이었다. 각각의 재료에 대해 샘플을 4개의 그룹으로 나누었다. 산성 조건 그룹은 pH 4.4, 5.4, 6.4의 부티르산 조건에서, 대조군 그룹은 pH 7.4의 인산완충식염수 조건에서 4일간 $37^{\circ}C$에서 보관하였다. 이후 압출강도를 측정하고 표면 형태를 분석하였다. Biodentine$^{(R)}$과 Theracal$^{(R)}$은 모든 산성 조건에서 ProRoot MTA$^{(R)}$ 보다 더 높은 압출강도를 보였고 pH 감소에 따라 압출강도가 감소하였다. 주사전자현미경을 이용한 관찰 결과 재료들 모두 산성 조건에서 표면 형태에 상당한 변화를 보였다. 결론적으로, Biodentine$^{(R)}$과 Theracal$^{(R)}$은 ProRoot MTA$^{(R)}$와 비교하여 더 높은 압출강도를 보였다. 또한 산성 조건은 규산삼칼슘 재료들의 압출강도와 미세구조를 약화시킬 수 있다.

• Bulletin of the Korean Chemical Society
• /
• 제33권7호
• /
• pp.2423-2426
• /
• 2012

• Computers and Concrete
• /
• 제15권1호
• /
• pp.89-101
• /
• 2015

In this paper, Artificial Neural Networks (ANN) and Multiple Linear Regression (MLR) models were discussed to determine the compressive strength of clinker mortars cured for 1, 2, 7 and 28 days. In the experimental stage, 1288 mortar samples were produced from 322 different clinker specimens and compressive strength tests were performed on these samples. Chemical properties of the clinker samples were also determined. In the modeling stage, these experimental results were used to construct the models. In the models tricalcium silicate ($C_3S$), dicalcium silicate ($C_2S$), tricalcium aluminate ($C_3A$), tetracalcium alumina ferrite ($C_4AF$), blaine values, specific gravity and age of samples were used as inputs and the compressive strength of clinker samples was used as output. The approximate reasoning ability of the models compared using some statistical parameters. As a result, ANN has shown satisfying relation with experimental results and suggests an alternative approach to evaluate compressive strength estimation of clinker mortars using related inputs. Furthermore MLR model showed a poor ability to predict.

• 한국세라믹학회지
• /
• 제23권5호
• /
• pp.35-40
• /
• 1986

The early hydration of tri-calcium silicate $(C_3S)$ with different cooling conditions was studied by varing water/solid ratio and atmosphere. The cooling condition and water/solid ratio affected to the second peak of heat liberation but it had no correlation to the induction period. The $Ca^{2+}$ concentration in the aqueous solution was maximized at the starting point of the second peak of heat liberation but in the $CO_2$ exsistence the $Ca^{2+}$ concentration was low and $SiO_2$ con-centration was increased. The hydration rate of $C_3S$ was so accelerated that the induction period could not appear in the $CO_2$ exsistence.